Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 60.0 - 70.0 MPa | 8700 - 10200 psi | Type 1B, 50mm/min; ISO 527-1/2:1993 |
Nylacast Cast Nylon 6, Glass Filled Information provided by Nylacast Ltd. |
|||
Tensile Strength, Yield | 60.0 - 70.0 MPa | 8700 - 10200 psi | Type 1B, 50mm/min; ISO 527-1/2:1993 |
Nylacast Impact Nylon 6, Impact Grade Nylacast Impact has been designed for applications that have a high impact resistance and noise reduction capabilities. It works more effectively in applications where there are high stress. It also.. |
|||
Tensile Strength, Yield | 60.0 - 70.0 MPa | 8700 - 10200 psi | ISO.527 DN.53455 |
Polimersan Plastics POLIPA® (PA 6) Polyamide POLIPA® PA6 (POLYAMIDE) is produced by poly condensation of e-aminoacid and by the help of d-carbon acid and d-amine poly condensation. Its characteristics depend upon the numbers of the main struc.. |
|||
Tensile Strength, Yield | 60.0 - 70.0 MPa | 8700 - 10200 psi | Injection; ISO 527 |
Raschig Group 2567 AMC Glass fiber-reinforced and inorganically filled polyester molding compound (UP) in various colors. Outstanding mechanical strength similar to BMC/SMC, very good electrical isolation properties and .. |
|||
Tensile Strength, Yield | 60.0 - 70.0 MPa | 8700 - 10200 psi | Injection; ISO 527 |
Raschig Group 2568 AMC Glass fiber-reinforced polyester molding compound. Very good mechanical strength, very good electrical properties and dimensional stability, heat resistant up to 500°C for short time - usable for s.. |
|||
Tensile Strength, Yield | 60.0 - 70.0 MPa | 8700 - 10200 psi | Injection; ISO 527 |
Raschig Group 2572 AMC Glass fiber reinforced Polyester molding compound. Very good mechanical strength, very good electrical properties and dimensional stability, good abrasion stability, high flame retardance in combin.. |
|||
Tensile Strength, Yield | 60.0 - 70.0 MPa | 8700 - 10200 psi | Injection and Compression; ISO 527 |
Raschig Group 3505 Epoxy Glass-fiber reinforced epoxy molding compound. Good mechanical strength, very good electrical isolation properties and dimensional stability even at high temperatures. This product meets the allowed.. |
|||
Tensile Strength, Yield | 60.0 - 70.0 MPa | 8700 - 10200 psi | Injection and Compression; ISO 527 |
Raschig Group 3535 Epoxy Glass fiber-reinforced epoxy molding compound. Good mechanical strength, very good electrical isolation properties adn dimensional stability even at high temperatures. Form: Low dust granulate pack.. |
|||
Tensile Strength, Yield | 60.0 - 70.0 MPa | 8700 - 10200 psi | Injection and Compression; ISO 527 |
Raschig Group 3536 Epoxy Glass-fiber reinforced epoxy molding compound. Good mechanical strength, very good electrical isolation properties and dimensional stability even at high temperatures. This product meets the allowed.. |
|||
Tensile Strength, Yield | 40.0 - 70.0 MPa | 5800 - 10200 psi | Injection; ISO 527 |
Raschig Group RALUPOL® 4385 UP Glass-fiber reinforced polyester molding compound. Low mold shrinkage and post-shrinkage, very high arc resistance, very high mechanical values. This product meets the allowed upper limits for heavy.. |
|||
Tensile Strength, Yield | 40.0 - 70.0 MPa | 5800 - 10200 psi | Injection; ISO 527 |
Raschig Group RALUPOL® 4806 UP Glass-fiber reinforced polyester molding compound. Very low mold shrinkage and post-shrinkage, very good mechanical strength, very good electrical values, better performance values compared to UP 80.. |
|||
Tensile Strength, Yield | 60.0 - 70.0 MPa | 8700 - 10200 psi | ISO.527 DN.53455 |
Polimersan Plastics POLIPA® (PA 6) Polyamide POLIPA® PA6 (POLYAMIDE) is produced by poly condensation of e-aminoacid and by the help of d-carbon acid and d-amine poly condensation. Its characteristics depend upon the numbers of the main struc.. |
|||
Tensile Strength, Yield | 30.0 - 70.0 MPa | 4350 - 10200 psi | Average value: 47.9 MPa Grade Count:34 |
Overview of materials for Acetal Homopolymer, Unreinforced, Impact Grade This property data is a summary of similar materials in the MatWeb database for the category "Acetal Homopolymer, Unreinforced, Impact Grade". Each property range of values reported is minimum and m.. |
|||
Tensile Strength, Yield | 40.0 - 70.0 MPa | 5800 - 10200 psi | Injection; ISO 527 |
Raschig Group RALUPOL® 8601 UP Glass-fiber reinforced polyester molding compound. Mold shrinkage similar to phenolic moulding compounds, low post-shrinkage, good electrical values, excellent heat resistance, good mechanical stren.. |
|||
Tensile Strength, Yield | 40.0 - 70.0 MPa | 5800 - 10200 psi | Injection; ISO 527 |
Raschig Group RALUPOL® 8602 UP Glass-fiber reinforced polyester molding compound. Mold shrinkage similar to phenolic molding compounds, low post-shrinkage, good electrical values, excellent heat resistance, good mechanical streng.. |
|||
Tensile Strength, Yield | 40.0 - 70.0 MPa | 5800 - 10200 psi | Injection; ISO 527 |
Raschig Group SURAPLAST 54 UPA Glass fiber reinforced polyester molding compound. Minimal mold shrinkage and post-shrinkage, very good arc resistance, very good mechanical strength. This product meets the allowed upper limits for.. |
|||
Tensile Strength, Yield | 50.0 - 70.0 MPa | 7250 - 10200 psi | Injection; ISO 527 |
Raschig Group SURAPLAST UPA 63 UP Glass fiber reinforced polyester molding compound. Minimal mold shrinkage and post-shrinkage, very good arc resistance, very good mechanical strength. This product meets the allowed upper limits for.. |
|||
Tensile Strength, Yield | 58.6 - 70.0 MPa | 8500 - 10200 psi | Average value: 63.7 MPa Grade Count:34 |
Overview of materials for Polycarbonate, Extruded This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate, Extruded". Each property range of values reported is minimum and maximum values of approp.. |
|||
Tensile Strength, Yield | 34.0 - 70.0 MPa | 4930 - 10200 psi | Average value: 53.9 MPa Grade Count:117 |
Overview of materials for Polycarbonate/PET Polyester Blend This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate/PET Polyester Blend". Each property range of values reported is minimum and maximum values.. |
|||
Tensile Strength, Yield | 41.4 - 70.0 MPa | 6000 - 10200 psi | Average value: 52.8 MPa Grade Count:13 |
Overview of materials for Acetal Homopolymer, PTFE-Filled This property data is a summary of similar materials in the MatWeb database for the category "Acetal Homopolymer, PTFE-Filled". Each property range of values reported is minimum and maximum values o.. |
|||
Tensile Strength, Yield | 50.0 - 70.0 MPa | 7250 - 10200 psi | Injection; ISO 527 |
Raschig Group MELOPLAS® 180 MF Wood flour-reinforced, phenol-modified MF molding compound (MPF) in dark colors. High surface hardness, good mechanical strength and electrical properties, good heat resistance. Self-extinguishing .. |
|||
Tensile Strength, Yield | 1.80 - 70.0 MPa | 261 - 10200 psi | Average value: 14.2 MPa Grade Count:104 |
Overview of materials for Thermoplastic Polyurethane (TPUR), Polyether Grade This property data is a summary of similar materials in the MatWeb database for the category "Thermoplastic Polyurethane (TPUR), Polyether Grade". Each property range of values reported is minimum a.. |
|||
Tensile Strength, Yield | 13.0 - 70.0 MPa | 1890 - 10200 psi | Average value: 24.7 MPa Grade Count:45 |
Overview of materials for Polypropylene with 30% Calcium Carbonate (CaCO3) Filler This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with 30% Calcium Carbonate (CaCO3) Filler". Each property range of values reported is mini.. |