Qualchem Danamid AFGFS2HUV30 Polyamide 66, 30% Glass Fiber
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | Qualchem Zrt. |
| Trade Name | Danamid |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Qualchem Danamid AFGFS2HUV30 Polyamide 66, 30% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Reinforced with glass fiber. Impact modified, heat and UV stabilized, for long-lasting use at 120-140°C, resistant to artificial lights.Information provided by Qualchem Zrt.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.33 g/cc | 0.0480 lb/in³ | DIN 53479 |
| Filler Content | 28 - 32 % | 28 - 32 % |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | >= 75.0 MPa | >= 10900 psi | 50 mm/min; ISO 527-1,2 |
| Elongation at Break | >= 4.0 % | >= 4.0 % | ISO 527-1,2 |
| Tensile Modulus | >= 7.80 GPa | >= 1130 ksi | ISO 527-1,2 |
| Charpy Impact Unnotched | >= 2.00 J/cm² @Temperature 23.0 °C |
>= 9.52 ft-lb/in² @Temperature 73.4 °F |
DIN 53453 |
| Charpy Impact, Notched | >= 0.500 J/cm² @Temperature 23.0 °C |
>= 2.38 ft-lb/in² @Temperature 73.4 °F |
DIN 53453 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 250 °C | 482 °F | DIN 53461 |
| Deflection Temperature at 1.8 MPa (264 psi) | 220 °C | 428 °F | DIN 53461 |
| Flammability, UL94 | HB @Thickness 4.00 mm |
HB @Thickness 0.157 in |
MSZ 10383 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | DIN 53482 |
| Comparative Tracking Index | 550 V | 550 V | IEC 112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Moisture Content | 2.0 - 2.2 % | 2.0 - 2.2 % | DIN 53714 |
Users viewing this material also viewed the following:
- Precision Polymer Engineering Z60B Hydrogenated NBR Compound
- Kazanorgsintez High Purity Argon
- Huntsman AVALON® 65 AB Thermoplastic Polyurethane
- Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 4.8 mm thick sheet
- Solvay Chemicals (CsAlF4) Cesium Tetrafluoroaluminate
- Techmer ES HiFill® PA6 GF33 L NAT024 33% Glass Filled
- Suzhou Hipro Polymers Hiprolon® 11 PFB Colorized Nylon powder
- A. Schulman CP814-01 Linear, Low-Density Polyethylene
- AK Steel ASTM A 1011, Class 2 Formable, Grade 60K Hot Rolled Carbon Steel, Medium/High Strength Low Alloy Steel (HSLA)
- 3M Dyneon™ TFM™ 1700 Modified PTFE Powder
Copyright © lookpolymers.com All Rights Reserved