Kolon KOCETAL® WR701 Wear Modified Acetal Resin
| Category | Polymer , Thermoplastic , Acetal (POM) |
| Manufacturer | Kolon |
| Trade Name | Kocetal® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Kolon KOCETAL® WR701 Wear Modified Acetal Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Improved weather resistant and easy flow grade. Applications: Weather resistant products. Information provided by API-Kolon.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.41 g/cc | 1.41 g/cc | ASTM D792 |
| Moisture Absorption at Equilibrium | 0.22 % | 0.22 % | 60% RH; ASTM D570 |
| Linear Mold Shrinkage | 0.020 cm/cm | 0.020 in/in | ASTM D955 |
| Melt Flow | 31 g/10 min | 31 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 80 | 80 | ASTM D785 |
| Tensile Strength | 63.0 MPa | 9140 psi | ASTM D638 |
| Elongation at Break | 45 % | 45 % | ASTM D638 |
| Flexural Strength | 87.0 MPa | 12600 psi | ASTM D790 |
| Flexural Modulus | 2.45 GPa | 355 ksi | ASTM D790 |
| Izod Impact, Notched | 0.600 J/cm | 1.12 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 130 µm/m-°C | 72.2 µin/in-°F | ASTM D696 |
| Melting Point | 166 °C | 331 °F | ASTM D1525 |
| Deflection Temperature at 0.46 MPa (66 psi) | 158 °C | 316 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 110 °C | 230 °F | ASTM D648 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+11 ohm-cm | 1.00e+11 ohm-cm | ASTM D257 |
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | ASTM D257 |
| Dielectric Constant | 3.7 | 3.7 | ASTM D150 |
| Dielectric Strength | 19.0 kV/mm | 483 kV/in | ASTM D149 |
| Dissipation Factor | 0.060 @Frequency 1.00e+6 Hz |
0.060 @Frequency 1.00e+6 Hz |
ASTM D150 |
Users viewing this material also viewed the following:
- S&E Specialty Polymers GR-1409 PVC
- S&E Specialty Polymers TufFill NH™ GTPO8290-36 TPO
- Lehmann & Voss LUVOCOM® 1500-0871 Polysulfone, with glass spheres
- LTL Color Compounds ColorFast® PBA2000 PBT/ABS Alloy, Flame Retarded
- LyondellBasell Astryn 65F4-3 Polypropylene Homopolymer, 30% Talc
- Spartech M60450 General Purpose PVC
- Techmer ES HiFill® POM CO GF20 CC 20% Glass Filled
- DuPont Performance Polymers Rynite® FR530 NC010 Polyethylene Terephthalate (PET) (Unverified Data**)
- Ascend Performance Materials Vydyne® 47 NT Nylon 66, Impact Modified, DAM
- Plansee MLR Molybdenum-Lanthanum Oxide; Recrystallized
Copyright © lookpolymers.com All Rights Reserved