Premix Thermoplastics PRE-ELEC® 12-000

Category	Polymer , Thermoplastic , Acetal (POM)
Manufacturer	Premix Thermoplastics Inc.
Trade Name	PRE-ELEC®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Premix Thermoplastics PRE-ELEC® 12-000.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

PRE-ELEC 12-000 is a conductive thermoplastic compound based on a polyacetal copolymer. Conductivity is achieved by using special carbon black. In addition to a low resistivity PRE-ELEC 12-000 has an excellent balance of mechanical properties with good impact strength. PRE-ELEC 12-000 is easy to extrude or injection mold. Test Specimen - 4.0 mm thick, 10.0 mm wide molded rod.Information provided by Premix Thermoplastics Inc.

Physical Properties	Metric	English	Comments
Density	1.44 g/cc	0.0520 lb/in³
Linear Mold Shrinkage	0.020 - 0.025 cm/cm	0.020 - 0.025 in/in	ISO 294-4

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	45.0 MPa	6530 psi	ISO 527
Elongation at Break	6.0 %	6.0 %	ISO 527
Tensile Modulus	3.40 GPa	493 ksi	ISO 527
Izod Impact, Notched	0.690 J/cm @Thickness 4.00 mm, Temperature 23.0 °C	1.29 ft-lb/in @Thickness 0.157 in, Temperature 73.4 °F	ISO 180
Izod Impact, Unnotched	7.40 J/cm @Thickness 4.00 mm, Temperature 23.0 °C	13.9 ft-lb/in @Thickness 0.157 in, Temperature 73.4 °F	ISO 180

Thermal Properties	Metric	English	Comments
Deflection Temperature at 1.8 MPa (264 psi)	82.0 °C	180 °F	ISO 75/Method Af

Electrical Properties	Metric	English	Comments
Volume Resistivity	<= 1000 ohm-cm	<= 1000 ohm-cm	ISO D-257
Surface Resistance	<= 1e+05	<= 1e+05	ISO D-257
Static Decay	<= 2.0 sec	<= 2.0 sec	ISO IEC 61340-5-1

Processing Properties	Metric	English	Comments
Melt Temperature	185 - 210 °C	365 - 410 °F
Mold Temperature	80.0 - 105 °C	176 - 221 °F
Drying Temperature	80.0 °C @Time 10800 - 14400 sec	176 °F @Time 3.00 - 4.00 hour	Pre-drying in a dehumidifier
Injection Pressure	60.0 - 80.0 MPa	8700 - 11600 psi

Descriptive Properties	Value	Comments
Injection Speed	Moderate