DuPont Performance Polymers Rynite® FR543 NC010 PET

Category Polymer , Thermoplastic , Polyester, TP , Polyethylene Terephthalate (PET) , Polyethylene Terephthalate (PET), 40% Glass Reinforced
Manufacturer DuPont Performance Polymers
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Rynite® FR543 NC010 PET.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Rynite® FR543 NC010 is a flame retardant, 43% glass reinforced polyethylene terephthalate. Has a 155C temperature index that is equivalent to many thermosets. Recognized by UL as UL94V-0 at 0.8mm(0.03in).Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Specific Gravity 1.79 g/cc
1.79 g/cc
ASTM D792
Density 1.79 g/cc
0.0647 lb/in³
ISO 1183
Filler Content 43 %
43 %
Water Absorption 0.060 %

@Temperature 23.0 °C
 0.060 %

@Temperature 73.4 °F
 50%RH,23°C,24h; ASTM D570
0.11 %

@Temperature 23.0 °C
 0.11 %

@Temperature 73.4 °F
 Equilibrium 50%RH; ISO 62, Similar to
0.62 %

@Temperature 23.0 °C
 0.62 %

@Temperature 73.4 °F
 Saturation, immersed; ISO 62, Similar to
Linear Mold Shrinkage 0.0013 cm/cm

@Thickness 1.57 mm
 0.0013 in/in

@Thickness 0.0618 in
 Flow
0.0020 cm/cm

@Thickness 3.20 mm
 0.0020 in/in

@Thickness 0.126 in
 Flow
0.0048 cm/cm

@Thickness 1.57 mm
 0.0048 in/in

@Thickness 0.0618 in
 Transverse
0.0065 cm/cm

@Thickness 3.20 mm
 0.0065 in/in

@Thickness 0.126 in
 Transverse
Linear Mold Shrinkage, Flow 0.0025 cm/cm
0.0025 in/in
Annealed; ISO 294-4
0.0020 cm/cm

@Thickness 2.00 mm
 0.0020 in/in

@Thickness 0.0787 in
 ISO 294-4
Linear Mold Shrinkage, Transverse 0.0105 cm/cm
0.0105 in/in
Annealed; ISO 294-4
0.0075 cm/cm

@Thickness 2.00 mm
 0.0075 in/in

@Thickness 0.0787 in
 ISO 294-4
Melt Index of Compound 6.0 g/10 min

@Load 2.16 kg,
Temperature 280 °C
 6.0 g/10 min

@Load 4.76 lb,
Temperature 536 °F
 cm3/10 min; ISO 1133
Mechanical Properties Metric English Comments
Hardness, Rockwell M 95
95
ASTM D785
102
102
ISO 2039/2
Hardness, Rockwell R 120
120
ASTM D785
122
122
ISO 2039/2
Tensile Strength at Break 170 MPa

@Temperature 23.0 °C
 24700 psi

@Temperature 73.4 °F
 ISO 527
Tensile Strength 55.2 MPa

@Temperature 150 °C
 8010 psi

@Temperature 302 °F
 ASTM D638
86.5 MPa

@Temperature 90.0 °C
 12500 psi

@Temperature 194 °F
 ASTM D638
172 MPa

@Temperature 23.0 °C
 24900 psi

@Temperature 73.4 °F
 ASTM D638
210 MPa

@Temperature -40.0 °C
 30500 psi

@Temperature -40.0 °F
 ASTM D638
Tensile Stress 22.4 MPa

@Strain 0.470 %,
Temperature 150 °C
 3250 psi

@Strain 0.470 %,
Temperature 302 °F
 ISO 527
27.22 MPa

@Strain 0.430 %,
Temperature 120 °C
 3948 psi

@Strain 0.430 %,
Temperature 248 °F
 ISO 527
27.5 MPa

@Strain 0.160 %,
Temperature 0.000 °C
 3990 psi

@Strain 0.160 %,
Temperature 32.0 °F
 ISO 527
28.39 MPa

@Strain 0.350 %,
Temperature 90.0 °C
 4118 psi

@Strain 0.350 %,
Temperature 194 °F
 ISO 527
29.0 MPa

@Strain 0.140 %,
Temperature -40.0 °C
 4210 psi

@Strain 0.140 %,
Temperature -40.0 °F
 ISO 527
30.0 MPa

@Strain 0.210 %,
Temperature 40.0 °C
 4350 psi

@Strain 0.210 %,
Temperature 104 °F
 ISO 527
31.0 MPa

@Strain 0.180 %,
Temperature 23.0 °C
 4500 psi

@Strain 0.180 %,
Temperature 73.4 °F
 ISO 527
34.9 MPa

@Strain 0.940 %,
Temperature 150 °C
 5060 psi

@Strain 0.940 %,
Temperature 302 °F
 ISO 527
35.57 MPa

@Strain 0.310 %,
Temperature 60.0 °C
 5159 psi

@Strain 0.310 %,
Temperature 140 °F
 ISO 527
41.5 MPa

@Strain 1.41 %,
Temperature 150 °C
 6020 psi

@Strain 1.41 %,
Temperature 302 °F
 ISO 527
41.8 MPa

@Strain 0.830 %,
Temperature 120 °C
 6060 psi

@Strain 0.830 %,
Temperature 248 °F
 ISO 527
45.7 MPa

@Strain 1.87 %,
Temperature 150 °C
 6630 psi

@Strain 1.87 %,
Temperature 302 °F
 ISO 527
47.19 MPa

@Strain 0.690 %,
Temperature 90.0 °C
 6844 psi

@Strain 0.690 %,
Temperature 194 °F
 ISO 527
49.1 MPa

@Strain 2.34 %,
Temperature 150 °C
 7120 psi

@Strain 2.34 %,
Temperature 302 °F
 ISO 527
50.35 MPa

@Strain 0.370 %,
Temperature 40.0 °C
 7303 psi

@Strain 0.370 %,
Temperature 104 °F
 ISO 527
50.8 MPa

@Strain 1.23 %,
Temperature 120 °C
 7370 psi

@Strain 1.23 %,
Temperature 248 °F
 ISO 527
51.7 MPa

@Strain 2.81 %,
Temperature 150 °C
 7500 psi

@Strain 2.81 %,
Temperature 302 °F
 ISO 527
52.4 MPa

@Strain 0.320 %,
Temperature 0.000 °C
 7600 psi

@Strain 0.320 %,
Temperature 32.0 °F
 ISO 527
53.8 MPa

@Strain 3.28 %,
Temperature 150 °C
 7800 psi

@Strain 3.28 %,
Temperature 302 °F
 ISO 527
53.9 MPa

@Strain 0.280 %,
Temperature -40.0 °C
 7820 psi

@Strain 0.280 %,
Temperature -40.0 °F
 ISO 527
55.0 MPa

@Strain 0.520 %,
Temperature 60.0 °C
 7980 psi

@Strain 0.520 %,
Temperature 140 °F
 ISO 527
55.6 MPa

@Strain 3.75 %,
Temperature 150 °C
 8060 psi

@Strain 3.75 %,
Temperature 302 °F
 ISO 527
56.4 MPa

@Strain 0.350 %,
Temperature 23.0 °C
 8180 psi

@Strain 0.350 %,
Temperature 73.4 °F
 ISO 527
56.85 MPa

@Strain 1.63 %,
Temperature 120 °C
 8245 psi

@Strain 1.63 %,
Temperature 248 °F
 ISO 527
57.1 MPa

@Strain 4.21 %,
Temperature 150 °C
 8280 psi

@Strain 4.21 %,
Temperature 302 °F
 ISO 527
58.5 MPa

@Strain 4.69 %,
Temperature 150 °C
 8480 psi

@Strain 4.69 %,
Temperature 302 °F
 ISO 527
59.61 MPa

@Strain 1.03 %,
Temperature 90.0 °C
 8646 psi

@Strain 1.03 %,
Temperature 194 °F
 ISO 527
61.26 MPa

@Strain 2.04 %,
Temperature 120 °C
 8885 psi

@Strain 2.04 %,
Temperature 248 °F
 ISO 527
64.62 MPa

@Strain 2.44 %,
Temperature 120 °C
 9372 psi

@Strain 2.44 %,
Temperature 248 °F
 ISO 527
67.28 MPa

@Strain 2.84 %,
Temperature 120 °C
 9758 psi

@Strain 2.84 %,
Temperature 248 °F
 ISO 527
68.2 MPa

@Strain 1.37 %,
Temperature 90.0 °C
 9890 psi

@Strain 1.37 %,
Temperature 194 °F
 ISO 527
69.36 MPa

@Strain 3.24 %,
Temperature 120 °C
 10060 psi

@Strain 3.24 %,
Temperature 248 °F
 ISO 527
71.09 MPa

@Strain 3.65 %,
Temperature 120 °C
 10310 psi

@Strain 3.65 %,
Temperature 248 °F
 ISO 527
71.87 MPa

@Strain 0.730 %,
Temperature 60.0 °C
 10420 psi

@Strain 0.730 %,
Temperature 140 °F
 ISO 527
72.35 MPa

@Strain 4.05 %,
Temperature 120 °C
 10490 psi

@Strain 4.05 %,
Temperature 248 °F
 ISO 527
72.8 MPa

@Strain 0.560 %,
Temperature 40.0 °C
 10600 psi

@Strain 0.560 %,
Temperature 104 °F
 ISO 527
74.5 MPa

@Strain 0.480 %,
Temperature 23.0 °C
 10800 psi

@Strain 0.480 %,
Temperature 73.4 °F
 ISO 527
74.52 MPa

@Strain 1.70 %,
Temperature 90.0 °C
 10810 psi

@Strain 1.70 %,
Temperature 194 °F
 ISO 527
75.5 MPa

@Strain 0.420 %,
Temperature -40.0 °C
 11000 psi

@Strain 0.420 %,
Temperature -40.0 °F
 ISO 527
75.9 MPa

@Strain 0.470 %,
Temperature 0.000 °C
 11000 psi

@Strain 0.470 %,
Temperature 32.0 °F
 ISO 527
79.34 MPa

@Strain 2.04 %,
Temperature 90.0 °C
 11510 psi

@Strain 2.04 %,
Temperature 194 °F
 ISO 527
83.14 MPa

@Strain 2.41 %,
Temperature 90.0 °C
 12060 psi

@Strain 2.41 %,
Temperature 194 °F
 ISO 527
83.19 MPa

@Strain 0.940 %,
Temperature 60.0 °C
 12070 psi

@Strain 0.940 %,
Temperature 140 °F
 ISO 527
85.76 MPa

@Strain 2.75 %,
Temperature 90.0 °C
 12440 psi

@Strain 2.75 %,
Temperature 194 °F
 ISO 527