- Polyram RamLloy PZF301G4 PC/PBT Alloy, 20% Glass Fiber
Polyram RamLloy PZF301G4 PC/PBT Alloy, 20% Glass Fiber
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/Polybutylene Terephthalate (PBT) Blend, Glass Filled , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | Polyram |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyram RamLloy PZF301G4 PC/PBT Alloy, 20% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
20% Glass fiber reinforced, impact modified PC/PBT alloy for injection molding applications.Information provided by Polyram.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.40 g/cc | 0.0506 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.0030 - 0.0050 cm/cm | 0.0030 - 0.0050 in/in | ISO 2577 |
| Melt Flow | 15 g/10 min @Load 2.16 kg, Temperature 275 °C |
15 g/10 min @Load 4.76 lb, Temperature 527 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 100 MPa | 14500 psi | ISO 527 |
| Elongation at Break | 2.5 % | 2.5 % | ISO 527 |
| Tensile Modulus | 6.60 GPa | 957 ksi | ISO 527 |
| Flexural Strength | 120 MPa | 17400 psi | ISO 178 |
| Flexural Modulus | 6.80 GPa | 986 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 8.00 kJ/m² @Temperature -30.0 °C |
3.81 ft-lb/in² @Temperature -22.0 °F |
ISO 180 |
| 10.0 kJ/m² @Temperature 23.0 °C |
4.76 ft-lb/in² @Temperature 73.4 °F |
ISO 180 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 195 °C | 383 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 135 °C | 275 °F | ISO 75 |
| Flammability, UL94 | HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
|
| Glow Wire Test | 850 °C | 1560 °F | GWFI; IEC 60695 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 3.5 @Frequency 1.00e+6 Hz |
3.5 @Frequency 1.00e+6 Hz |
IEC 60250 |
Users viewing this material also viewed the following:
- Karina E 48/23-RG-PO Black Color Concentrate for PVC
- Lehmann & Voss LUVOCOM® 1/GF/30/TF/15 Polyamide 66, with glass fiber and PTFE, heat stabilized
- Solvay Specialty Polymers Galden® D05 PFPE Fluid
- Polyplastics Duranex® 6302T Polybutylene Terephthalate (PBT), Low friction, Low wear, Mineral filled
- Williams Advanced Alloys WS310 Solder
- Diamond Polymers ASA T-105
- Fainplast Compounds HAX HF 019/27 Halogen Free PVC
- Dow Corning 200® 1.5 CST FLUID
- EMS-Grivory Grivory® LBV-30H FWA nat PA12-GF30
Copyright © lookpolymers.com All Rights Reserved