Polyplastic Armamid® PA GF25-1FR Nylon 6, 25% Glass Fiber
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled , Nylon 6, Glass Fiber Filled, Flame Retardant |
| Manufacturer | Polyplastic Group |
| Trade Name | Armamid® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyplastic Armamid® PA GF25-1FR Nylon 6, 25% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Flame retardant, RoHS compliantInformation provided by PolyPlastic Group.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.60 g/cc | 0.0578 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | <= 0.0020 cm/cm | <= 0.0020 in/in | |
| Linear Mold Shrinkage, Flow | 0.0015 - 0.0025 cm/cm | 0.0015 - 0.0025 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0060 - 0.0090 cm/cm | 0.0060 - 0.0090 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 130 MPa | 18900 psi | ISO 37 |
| Elongation at Break | 3.0 % | 3.0 % | ISO 37 |
| Flexural Strength | 180 MPa | 26100 psi | ISO 178 |
| Flexural Modulus | 8.00 GPa | 1160 ksi | ISO 178 |
| Charpy Impact Unnotched | 4.00 J/cm² @Temperature 23.0 °C |
19.0 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 195 °C | 383 °F | ISO 75 |
| Flammability, UL94 | V-0 @Thickness 1.60 mm |
V-0 @Thickness 0.0630 in |
|
| Glow Wire Test | 960 °C @Thickness 1.60 mm |
1760 °F @Thickness 0.0630 in |
IEC 60695-2-1 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 |
| Dielectric Strength | 25.0 kV/mm | 635 kV/in | IEC 60243-1 |
| Comparative Tracking Index | 350 V | 350 V | IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 260 - 270 °C | 500 - 518 °F | |
| Mold Temperature | 90.0 °C | 194 °F | |
| Drying Temperature | 85.0 °C @Time 7200 - 14400 sec |
185 °F @Time 2.00 - 4.00 hour |
Users viewing this material also viewed the following:
- Saint-Gobain CHR® M705 Polyester Film Backing Acrylic Adhesive Pressure Sensitive Tape
- Struktol ZINC STEARATE CM
- SABIC Innovative Plastics LNP THERMOCOMP UFW49S PPA (Asia Pacific)
- Cossa Polimeri ESTABLEND 6500 A Polycarbonate ABS Blend
- Dow DOWLEX™ 2025G Linear Low Density Polyethylene
- AFE Technologies Cronite 657 Nickel Alloy Castings
- Arlon R33073X0085 0.0085" Cured Silicone Rubber with Fiberglass Substrate
- BASF Pentanol
- 3M 501+ Specialty High Temperature Masking Tape
- BASF Styropor® BF 222 EPS
Copyright © lookpolymers.com All Rights Reserved