Polymer Resources PPX-GP2 Modified-PPO, General Purpose
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polyphenylene Ether, Molded |
| Manufacturer | Polymer Resources, LTD |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polymer Resources PPX-GP2 Modified-PPO, General Purpose.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Modified-Polyphenylene Oxide, General Purpose, 250F HDTProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided by Polymer Resources Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.05 g/cc | 1.05 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | ASTM D955 |
| Melt Flow | 6.0 - 10 g/10 min @Load 11.6 kg, Temperature 250 °C |
6.0 - 10 g/10 min @Load 25.6 lb, Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 118 | 118 | ASTM D785 |
| Tensile Strength at Break | 53.4 MPa | 7750 psi | ASTM D638 |
| Tensile Strength, Yield | 56.9 MPa | 8250 psi | ASTM D638 |
| Elongation at Break | 30 % | 30 % | ASTM D638 |
| Flexural Strength | 79.3 MPa | 11500 psi | ASTM D790 |
| Flexural Modulus | 2.34 GPa | 340 ksi | ASTM D790 |
| Izod Impact, Notched | 1.33 J/cm @Temperature -30.0 °C |
2.50 ft-lb/in @Temperature -22.0 °F |
ASTM D256 |
| 2.14 J/cm @Temperature 22.8 °C |
4.00 ft-lb/in @Temperature 73.0 °F |
ASTM D256 | |
| Charpy Impact, Notched | 1.47 J/cm² @Temperature 22.8 °C |
7.00 ft-lb/in² @Temperature 73.0 °F |
ISO 179/1eA |
| Gardner Impact | 16.9 J | 12.5 ft-lb | ASTM D3029 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 121 °C | 250 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 116 °C | 240 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.59 mm |
HB @Thickness 0.0626 in |
|
| HB @Thickness 3.17 mm |
HB @Thickness 0.125 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 249 - 299 °C | 480 - 570 °F | |
| Middle Barrel Temperature | 260 - 304 °C | 500 - 580 °F | |
| Front Barrel Temperature | 271 - 310 °C | 520 - 590 °F | |
| Melt Temperature | 282 - 310 °C | 540 - 590 °F | |
| Mold Temperature | 71.1 - 93.3 °C | 160 - 200 °F | |
| Drying Temperature | 104 - 110 °C | 220 - 230 °F | |
| Dry Time | 3.00 - 4.00 hour | 3.00 - 4.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Vent | 0.0015 |
Users viewing this material also viewed the following:
- MV Labs AG165 KAg(CN)2 Potassium dicyanoargentate(I)
- NOVA Chemicals Dylark® 232 High Performance Styrenic, Transparent Grade
- Northstar Polymers MAP-R06C Semi Rigid Structural Foam Formulation
- Fujipoly Industries Sarcon® 85GSR Thin-Film GSR
- JPJ Technologies PP C120 PP Copolymer Injection Molding
- Solvay MACKADET® EQ-112 Surfactant
- ConocoPhillips Syncon® EP Heavy Duty Grease NLGI 1
- Eagle Brass 519 Phosphor Bronzes 6%, 1/2 Hard
- DuPont Performance Polymers Crastin® LW9030 NC010 PBT+ASA (Unverified Data**)
- Fainplast Compounds HL 91/1 Flexible PVC, Insulation for High Temperatures
Copyright © lookpolymers.com All Rights Reserved