Aclo Accutech Polypropylene Copolymer CP0437W40L1 Wollastonite Reinforced
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Mineral Reinforced |
| Manufacturer | Aclo Compounders |
| Trade Name | Accutech |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aclo Accutech Polypropylene Copolymer CP0437W40L1 Wollastonite Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.22 g/cc | 0.0441 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0050 cm/cm | 0.0050 in/in | MD; ASTM D955 |
| Melt Flow | 18 g/10 min | 18 g/10 min | ASTM D1238 |
| Ash | 40 % | 40 % | ASTM D2584 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 43 | 43 | ASTM D785 |
| Tensile Strength at Break | 14.0 MPa | 2030 psi | ASTM D638 |
| Tensile Strength, Yield | 17.0 MPa | 2470 psi | ASTM D638 |
| Elongation at Break | 13 % | 13 % | ASTM D638 |
| Elongation at Yield | 3.0 % | 3.0 % | ASTM D638 |
| Tensile Modulus | 2.40 GPa | 348 ksi | ASTM D638 |
| Flexural Strength | 20.0 MPa | 2900 psi | ASTM D790 |
| Flexural Modulus | 2.299 GPa | 333.5 ksi | ASTM D790 |
| Izod Impact, Notched | 1.66 J/cm | 3.10 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 102 °C | 216 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 61.1 °C | 142 °F |
Users viewing this material also viewed the following:
- Nye Lubricants 503 (NT) Synthetic Oil
- SABIC Innovative Plastics Lexan® ML6413 PC
- Lehmann & Voss LUVOCOM® 20-7343 Polyphthalamide, with carbon fiber
- Star Plastics PC703 Molding Grade PC with release
- Uniseal BETABRACE™ 85076 Epoxy
- Loctite® Tak Pak® 444 Instant Adhesive
- Bales Mold Service AMS-2404-C, AMS-2405-B Mold Coating
- Akzo Nobel Expancel® 551 WU 20 Wet unexpanded microspheres
- 3M 9472LE Adhesive Transfer Tapes with Adhesive 300LSE
- Asahi Kasei Xyron® X0715 Modified Polyphenylene Ether
Copyright © lookpolymers.com All Rights Reserved