Lavergne VYPET VNT 635A PET 35% Glass Reinforced
| Category | Polymer , Thermoplastic , Polyester, TP , Polyethylene Terephthalate (PET) , Polyethylene Terephthalate (PET), 30% Glass Reinforced |
| Manufacturer | Lavergne Performance Compounds |
| Trade Name | VYPET |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lavergne VYPET VNT 635A PET 35% Glass Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Vypet 635A is a 35 % glass reinforced PET injection molding compound designed for electrical and structural applications with a very glossy surface.Features: High temperature performance, Excellent strength and stiffness, Quality A surfaceTypical Applications: Furniture Brackets/Connectors GrillsInformation provided by Bieglo Gmbh for Lavergne Performance Compounds
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.56 g/cc | 0.0564 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm @Thickness 2.00 mm |
0.0040 in/in @Thickness 0.0787 in |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm @Thickness 2.00 mm |
0.0080 in/in @Thickness 0.0787 in |
ASTM D955 |
| Ash | 35 % | 35 % | ASTM D2854 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 140 MPa | 20300 psi | 5 mm/min; ASTM D638 |
| Flexural Strength | 210 MPa | 30500 psi | 1.3 mm/min; ASTM D790 |
| Flexural Modulus | 10.0 GPa | 1450 ksi | 1.3 mm/min; ASTM D790 |
| Izod Impact, Notched | 0.750 J/cm @Temperature 23.0 °C |
1.41 ft-lb/in @Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 225 °C | 437 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 260 - 270 °C | 500 - 518 °F | |
| Middle Barrel Temperature | 265 - 275 °C | 509 - 527 °F | |
| Front Barrel Temperature | 270 - 295 °C | 518 - 563 °F | |
| Nozzle Temperature | 275 - 300 °C | 527 - 572 °F | |
| Melt Temperature | 275 - 300 °C | 527 - 572 °F | |
| Mold Temperature | 95.0 - 120 °C | 203 - 248 °F | |
| Injection Pressure | 55.0 - 85.0 MPa | 7980 - 12300 psi |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics LNP KONDUIT RTF2B PA 66 (Europe-Africa-Middle East)
- SABIC Innovative Plastics PC2200R PC (Asia Pacific)
- Techmer ES HiFill® PA6/6 L N MB Nylon 66
- A. Schulman POLYFLAM™ RPP 1133 Flame Retardant, Copolymer Polypropylene
- Polyram PlusTek PB302G50BK39D Nylon 6, 50% Glass Fiber Reinforced, UV and Heat Stabilized
- Cotronics Duralco™ 127 400°F (200°C) Graphite Filled Epoxy
- BASF Ultramid® A3Z PA66 (Conditioned)
- Plenco 7591 Phenolic, Pellet, Transfer Molded
Copyright © lookpolymers.com All Rights Reserved