PolyOne Edgetek® AT-30GB/000 Acetal-Copolymer, Glass Bead Filled (discontinued **)
| Category | Polymer , Thermoplastic , Acetal (POM) |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Edgetek® AT-30GB/000 Acetal-Copolymer, Glass Bead Filled
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description/Features:Glass Bead FilledInformation provided by PolyOne Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.63 g/cc | 1.63 g/cc | ASTM D792 |
| Water Absorption | 0.90 % @Thickness 3.17 mm |
0.90 % @Thickness 0.125 in |
24 hr. Immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0070 - 0.0090 cm/cm | 0.0070 - 0.0090 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 44.8 MPa | 6500 psi | Type 1 - Rigids, Yield, 0.2 in/min; ASTM D638 |
| Elongation at Break | 5.0 - 6.0 % | 5.0 - 6.0 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Tensile Modulus | 3.38 GPa | 490 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Flexural Strength | 62.1 MPa | 9000 psi | ASTM D790 |
| Flexural Modulus | 3.17 GPa | 460 ksi | ASTM D790 |
| Izod Impact, Notched | 0.374 J/cm @Thickness 3.17 mm, Temperature 23.0 °C |
0.700 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
Method A, Injection Molded; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 116 °C | 240 °F | Unannealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 193 - 210 °C | 380 - 410 °F | Molding |
Users viewing this material also viewed the following:
- Plaskolite Optix® CA - 51 HF OG General Purpose Acrylic Resin
- LG Chemical LUMID GN1001AF PA6, Halogen Free Flame Retardant
- Saint-Gobain Transflow® M-34-R Raw Milk Tubing Formulation
- Formosa Plastics Formolene® 3312E Random Copolymer Polypropylene
- CP-Polymer-Technik Wellamid® 6600 HWS Nylon 66, Finely Crystalline, Heat Stabilized, Conditioned
- Esstech X-829-0050 Adhesive Monomer PMGDM, 50% (w/w) Solution in Acetone, C32H34O16
- DuPont Performance Polymers Neoprene GW M1 Polychloroprene Rubber
- Fainplast Compounds MRT 256/G Medical Rigid PVC, Injection Molding
- Solvay Specialty Polymers Parmax® 1200 Self-Reinforcing Polyethersulfone (discontinued **)
- DuPont Nucrel® 0910HS-SR Ethylene-Methacrylic Acid Copolymer Resin for Extrusion Coating (discontinued **)<
Copyright © lookpolymers.com All Rights Reserved