- Polymer Resources PCSF-FR Polycarbonate, 5% Glass Reinforced Structural Foam Grade
Polymer Resources PCSF-FR Polycarbonate, 5% Glass Reinforced Structural Foam Grade
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, 10% Glass Filled , Polycarbonate, Foam Grade, Glass Filled , Polycarbonate, Glass Fiber Filled, Flame Retardant |
| Manufacturer | Polymer Resources, LTD |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polymer Resources PCSF-FR Polycarbonate, 5% Glass Reinforced Structural Foam Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Polycarbonate, 5% Glass Reinforced Structural Foam GradeFeatures: • Flame Retardant • Foamable • Self ExtinguishingProcess: Foam MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided by Polymer Resources Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.21 g/cc | 1.21 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | ASTM D955 |
| Melt Flow | 5.0 - 12 g/10 min @Load 1.20 kg, Temperature 300 °C |
5.0 - 12 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 58.6 MPa | 8500 psi | ASTM D638 |
| Tensile Strength, Yield | 55.8 MPa | 8100 psi | ASTM D638 |
| Flexural Strength | 96.5 MPa | 14000 psi | ASTM D790 |
| Flexural Modulus | 3.17 GPa | 460 ksi | ASTM D790 |
| Izod Impact, Notched | 1.60 J/cm @Temperature 22.8 °C |
3.00 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 138 °C | 280 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 131 °C | 268 °F | ASTM D648 |
| UL RTI, Electrical | 80.0 °C @Thickness 5.99 mm |
176 °F @Thickness 0.236 in |
UL 746 |
| UL RTI, Mechanical with Impact | 80.0 °C @Thickness 5.99 mm |
176 °F @Thickness 0.236 in |
UL 746 |
| UL RTI, Mechanical without Impact | 80.0 °C @Thickness 5.99 mm |
176 °F @Thickness 0.236 in |
UL 746 |
| Flammability, UL94 | V-0 @Thickness 6.00 mm |
V-0 @Thickness 0.236 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 254 - 266 °C | 490 - 510 °F | |
| Middle Barrel Temperature | 293 - 310 °C | 560 - 590 °F | |
| Front Barrel Temperature | 293 - 310 °C | 560 - 590 °F | |
| Melt Temperature | 288 - 316 °C | 550 - 600 °F | |
| Mold Temperature | 76.7 - 98.9 °C | 170 - 210 °F | |
| Drying Temperature | 118 - 124 °C | 245 - 255 °F | |
| Dry Time | 3.00 - 4.00 hour | 3.00 - 4.00 hour |
Users viewing this material also viewed the following:
- Plaskolite Optix® CA - 900 High Impact Grade Acrylic Resin
- Omni Plastics OmniLon™ 6 PA6 GR13 IM6 Glass Reinforced/Impact Modified Nylon
- LyondellBasell Petrothene® LR734001 High Density Polyethylene (Blow Molding Grade)
- LATI Latamid 66 H2 G/25-V0CT4 PA 66, 25% Glass Fiber Reinforced, Heat Stabilized, Flame Retardant
- Samsung Cheil Industries Starex® VG-4910 ABS, Glass Filled FR
- Borealis Borcoat™ EA165E Elastomer Modified Polypropylene for Extrusion
- Arkema Group Pebax® 7033 SP 01 Polyether Block Amide (PEBA)
- Arlon 48576R005 0.0055" (0.140 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate
- Loctite® Durabond® E-90FL Epoxy Adhesive
- DSM Stanyl® 46HF5050 Nylon 46-50% Glass Reinforced (European and Asian Grade) (Dry)
Copyright © lookpolymers.com All Rights Reserved