- Polymer Resources PC-GP1-D-[color]-6 Polycarbonate, FDA-compliant Feedstocks, Low Flow with Mold Release
Polymer Resources PC-GP1-D-[color]-6 Polycarbonate, FDA-compliant Feedstocks, Low Flow with Mold Release
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Molded |
| Manufacturer | Polymer Resources, LTD |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polymer Resources PC-GP1-D-[color]-6 Polycarbonate, FDA-compliant Feedstocks, Low Flow with Mold Release.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Polycarbonate, FDA-compliant Feedstocks, Low Flow with Mold ReleaseProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided by Polymer Resources Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | ASTM D955 |
| Melt Flow | 5.0 - 10 g/10 min @Load 1.20 kg, Temperature 300 °C |
5.0 - 10 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 72.4 MPa | 10500 psi | ASTM D638 |
| Tensile Strength, Yield | 62.1 MPa | 9000 psi | ASTM D638 |
| Flexural Strength | 96.5 MPa | 14000 psi | ASTM D790 |
| Flexural Modulus | 2.31 GPa | 335 ksi | ASTM D790 |
| Izod Impact, Notched | 9.08 J/cm @Temperature 22.8 °C |
17.0 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Gardner Impact | 36.2 J | 26.7 ft-lb | ASTM D3029 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 138 °C | 280 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 132 °C | 270 °F | ASTM D648 |
| Flammability, UL94 | V-2 @Thickness 1.50 mm |
V-2 @Thickness 0.0591 in |
|
| V-2 @Thickness 3.00 mm |
V-2 @Thickness 0.118 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 288 - 310 °C | 550 - 590 °F | |
| Middle Barrel Temperature | 299 - 321 °C | 570 - 610 °F | |
| Front Barrel Temperature | 310 - 332 °C | 590 - 630 °F | |
| Melt Temperature | 316 - 343 °C | 600 - 650 °F | |
| Mold Temperature | 82.2 - 116 °C | 180 - 240 °F | |
| Drying Temperature | 118 - 124 °C | 245 - 255 °F | |
| Dry Time | 3.00 - 4.00 hour | 3.00 - 4.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Vent | 0.0005 |
Users viewing this material also viewed the following:
- Plastcom PLASTALEN® PQ 81 N 003 Polypropylene with improved impact strength
- Mytex Polymers AS20LW Polypropylene, Talc filled, Compounded
- Chevron Phillips HiD® 9406 HDPE Blow Molding Resin (discontinued **)
- ICE Al2O3 99.5
- Lucent Polymers TPP-140 Polypropylene, Homopolymer, 40% Talc Filled
- Sichuan Deyang Haton® hp23310 Polyphenylene Sulfide Coating
- A. Schulman POLYBATCH™ Blue 40567 Concentrate Based In LDPE
- ExxonMobil SAE 30 Mobilgard 300
- 3D Systems DuraForm® AF Nylon for SLS® Systems
- Haynes Hastelloy® C-22® alloy, 6.4-19.1 mm thick plate, solution heat treated
Copyright © lookpolymers.com All Rights Reserved