- PolyOne Lubri-Tech™ ES-20GF/15T Polyethersulfone - 20% Glass Fiber Reinforced - 15% PTFE Lubricated (disconti
PolyOne Lubri-Tech™ ES-20GF/15T Polyethersulfone - 20% Glass Fiber Reinforced - 15% PTFE Lubricated (disconti
| Category | Polymer , Thermoplastic , Polyethersulfone (PES) |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Lubri-Tech™ ES-20GF/15T Polyethersulfone - 20% Glass Fiber Reinforced - 15% PTFE Lubricated
(disconti.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by PolyOne.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.60 g/cc | 0.0578 lb/in³ | ASTM D792 |
| Water Absorption | 0.30 % | 0.30 % | 24 hrs. ASTM D570 |
| Linear Mold Shrinkage | 0.0030 cm/cm @Thickness 3.17 mm |
0.0030 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 121 MPa | 17500 psi | ASTM D638 |
| Elongation at Break | 3.0 - 4.0 % | 3.0 - 4.0 % | ASTM D638 |
| Tensile Modulus | 6.20 GPa | 899 ksi | ASTM D638 |
| Flexural Yield Strength | 162 MPa | 23500 psi | ASTM D790 |
| Flexural Modulus | 5.70 GPa | 827 ksi | ASTM D790 |
| Compressive Yield Strength | 117 MPa | 17000 psi | ASTM D695 |
| Izod Impact, Notched | 0.850 J/cm @Thickness 6.35 mm |
1.59 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 354 - 382 °C | 669 - 720 °F | Stock |
| Mold Temperature | 121 - 149 °C | 250 - 300 °F | |
| Drying Temperature | 149 °C | 300 °F |
Users viewing this material also viewed the following:
- Polystrand ThermoPro™ IE6010 Unitape Unidirectional Polypropylene-Glass Composite
- Parker Chomerics CHO-FORM 5519 Conductive Silicone
- Raschig Group AMPLA® 2000 melamine-modified polyester
- Momentive Performance Materials Silplusâ„¢ 70 HS High Strength Heat Cured Rubber
- Haynes 25 alloy, cold worked sheet, 20% cold reduction, aged at 370°C (700°F) for 1 hour
- Samsung Cheil Industries Infino® AR-9301 PA, Glass Filled General Purpose
- SABIC Innovative Plastics LNP THERMOCOMP YH0235AC PE
- ConocoPhillips IGL-9 Enclosed Gear Lubricant ISO 680, AGMA Number 8EP
- Eurofoam Porocell POR 304 CM-S EPDM Foam
- 3M 4298UV Adhesion Promoter
Copyright © lookpolymers.com All Rights Reserved