Polymer Resources NY66-G20-MD Nylon 66, 20% Glass Reinforced with MoS2
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 20% Glass Fiber Filled , Nylon 66, MoS2 Filled |
| Manufacturer | Polymer Resources, LTD |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polymer Resources NY66-G20-MD Nylon 66, 20% Glass Reinforced with MoS2.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Nylon 66, 20% Glass Reinforced with Molybdenum Disulfide for Lubrication and WearProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylon grades are tested dry as molded (DAM).Information provided by Polymer Resources Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.38 g/cc | 1.38 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0030 - 0.013 cm/cm | 0.0030 - 0.013 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 145 MPa | 21000 psi | ASTM D638 |
| Tensile Strength, Yield | 145 MPa | 21000 psi | ASTM D638 |
| Flexural Strength | 228 MPa | 33000 psi | ASTM D790 |
| Flexural Modulus | 7.58 GPa | 1100 ksi | ASTM D790 |
| Izod Impact, Notched | 0.801 J/cm @Temperature 22.8 °C |
1.50 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 254 °C | 490 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 246 °C | 475 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.59 mm |
HB @Thickness 0.0626 in |
|
| HB @Thickness 3.17 mm |
HB @Thickness 0.125 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 266 - 288 °C | 510 - 550 °F | |
| Middle Barrel Temperature | 271 - 293 °C | 520 - 560 °F | |
| Front Barrel Temperature | 277 - 299 °C | 530 - 570 °F | |
| Melt Temperature | 285 - 304 °C | 545 - 580 °F | |
| Mold Temperature | 93.3 - 110 °C | 200 - 230 °F | |
| Drying Temperature | 73.9 - 85.0 °C | 165 - 185 °F | |
| Dry Time | 3.00 - 4.00 hour | 3.00 - 4.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Vent | 0.0005 |
Users viewing this material also viewed the following:
- Polimeri Europa Europrene® 1739 Emulsion Styrene-Butadiene Rubber
- Precision Polymer Engineering V75E Fluoroelastomer Compound
- Pearl Engineering PEPLPET B-113C PET Sheet Grade
- Michelman® Coating X300™ Plus Water based, moisture and water resistant coating
- A. Schulman SCHULAMID® 66 GF33 33% Glass Fiber Reinforced Nylon 66
- Toyobo VYLOPET® EMC133 Injection Molding Polyester Resin, Hydrolysis Resistant
- ChevronTexaco TEGRA® ISO 220 Synthetic Compressor Oil HC
- Assab Steels CORRAX Plastic Mold Material
- Beijing Evergrow Resources TBG Glass Fiber Tissue
- Resinlab® EP1300 Black Unfilled Electronic Grade Epoxy Encapsulant
Copyright © lookpolymers.com All Rights Reserved