Polymer Resources NY6-G13 Nylon 6, 13% Glass Reinforced

Category	Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 10% Glass Fiber Filled
Manufacturer	Polymer Resources, LTD
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Polymer Resources NY6-G13 Nylon 6, 13% Glass Reinforced.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Nylon 6, 13% Glass Reinforced, LubricatedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylon grades are tested dry as molded (DAM).Information provided by Polymer Resources Corporation.

Physical Properties	Metric	English	Comments
Specific Gravity	1.22 g/cc	1.22 g/cc	ASTM D792
Linear Mold Shrinkage	0.0040 - 0.0060 cm/cm	0.0040 - 0.0060 in/in	ASTM D955

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	131 MPa	19000 psi	ASTM D638
Tensile Strength, Yield	131 MPa	19000 psi	ASTM D638
Flexural Strength	165 MPa	24000 psi	ASTM D790
Flexural Modulus	5.24 GPa	760 ksi	ASTM D790
Izod Impact, Notched	0.587 J/cm @Temperature 22.8 °C	1.10 ft-lb/in @Temperature 73.0 °F	ASTM D256

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	204 °C	400 °F	ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	199 °C	390 °F	ASTM D648
Flammability, UL94	HB @Thickness 1.59 mm	HB @Thickness 0.0626 in
	HB @Thickness 3.17 mm	HB @Thickness 0.125 in

Processing Properties	Metric	English
Rear Barrel Temperature	249 - 268 °C	480 - 515 °F
Middle Barrel Temperature	243 - 260 °C	470 - 500 °F
Front Barrel Temperature	249 - 268 °C	480 - 515 °F
Melt Temperature	249 - 268 °C	480 - 515 °F
Mold Temperature	65.6 - 104 °C	150 - 220 °F
Drying Temperature	73.9 - 85.0 °C	165 - 185 °F
Dry Time	3.00 - 4.00 hour	3.00 - 4.00 hour

Descriptive Properties	Value	Comments
Vent	0.0005