Styron CALIBREâ„¢ 302V-10 Polycarbonate Resin
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | Styron |
| Trade Name | CALIBRE™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Styron CALIBREâ„¢ 302V-10 Polycarbonate Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Overview: CALIBREâ„¢ 300V Polycarbonate resins offer exceptional impact resistance, heat distortion resistance, optical clarity and meets UL94 V-2 rating. CALIBRE 300V series products are available in 3 additive packages: CALIBRE 301V: Mold release. CALIBRE 302V: UV stabilizer. CALIBRE 303V: Mold release and UV stabilizer.Govt. and Industry Standards: CSA (Canadian Standards Association)Underwriters Laboratory Inc. (UL) Applications:Electronic components LightingStorage Media HousingsInformation provided by Styron
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in³ | ISO 1183/B |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | ISO 294-4 |
| Melt Flow | 10 g/10 min @Load 1.20 kg, Temperature 300 °C |
10 g/10 min @Load 2.65 lb, Temperature 572 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 71.0 MPa | 10300 psi | ISO 527-2/50 |
| Tensile Strength, Yield | 60.0 MPa | 8700 psi | ISO 527-2/50 |
| Elongation at Break | 150 % | 150 % | ISO 527-2/50 |
| Elongation at Yield | 6.0 % | 6.0 % | ISO 527-2/50 |
| Tensile Modulus | 2.30 GPa | 334 ksi | ISO 527-2/50 |
| Flexural Strength | 97.0 MPa | 14100 psi | 3-point; ISO 178 |
| Flexural Modulus | 2.40 GPa | 348 ksi | 3-point; ISO 178 |
| Izod Impact, Notched | 9.00 J/cm @Temperature 23.0 °C |
16.9 ft-lb/in @Temperature 73.4 °F |
ISO 180/4A |
| Charpy Impact, Notched | 3.50 J/cm² @Temperature 23.0 °C |
16.7 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Hot Ball Pressure Test | 125 °C | 257 °F | IEC 60335-1 |
| Deflection Temperature at 0.46 MPa (66 psi) | 141 °C | 286 °F | Annealed; ISO 75-2/B |
| Deflection Temperature at 1.8 MPa (264 psi) | 122 °C | 252 °F | Unannealed; ISO 75-2/A |
| 138 °C | 280 °F | Annealed; ISO 75-2/A | |
| Vicat Softening Point | 146 °C | 295 °F | ISO 306/B50 |
| Flammability, UL94 | V-2 @Thickness 1.60 mm |
V-2 @Thickness 0.0630 in |
|
| V-2 @Thickness 3.20 mm |
V-2 @Thickness 0.126 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Comparative Tracking Index | 250 V @Thickness 2.00 mm |
250 V @Thickness 0.0787 in |
Solution A; IEC 60112 |
Users viewing this material also viewed the following:
- Network Polymers 707 Polystyrene
- Nilit FRIANYL B63 W-GV15 Nylon 6 for injection molding, 15% glass fiber reinforced
- Solvay Specialty Polymers Udel® P-1710 Polysulfone (PSU) (Unverified Data**)
- LATI Latan 13 S/30 POM, 30% Glass Bead Reinforced
- Sylvin Technologies 9925-85 Natural PVC Molding Compound
- Techmer ES HiFill® PA6 CM40 HS 40% Mineral Filled
- SABIC Innovative Plastics LNP STAT-KON PFD04S PA 6 (Europe-Africa-Middle East)
- CP-Polymer-Technik Wellamid® 6000 HWV0CP Nylon 6, Flame Protection, Heat Stabilized, Dry
- Axiall 8752 Moldings & Extrusions Flexible PVC
- Parker Chomerics CHO-SHIELD® 2052 Conductive Coating
Copyright © lookpolymers.com All Rights Reserved