SABIC Innovative Plastics ULTEM CRS5201R PEI (Europe-Africa-Middle East)

Category	Polymer , Thermoplastic , Polyetherimide (PEI)
Manufacturer	SABIC Innovative Plastics (GE Plastics)
Trade Name	ULTEM
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	SABIC Innovative Plastics ULTEM CRS5201R PEI (Europe-Africa-Middle East).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

20% Glass fiber filled, standard flow Polyetherimide copolymer (Tg 225C) with internal mold release and enhanced chemical resistance to strong acids, bases, aromatics, and ketones. Resin is RoHS compliant.

Physical Properties	Metric	English	Comments
Density	1.43 g/cc	0.0517 lb/inÂ³	ISO 1183
Moisture Absorption	0.200 %	0.200 %	23Â°C / 50% RH; ISO 62
Water Absorption at Saturation	1.0 %	1.0 %	ISO 62
Linear Mold Shrinkage, Flow	0.0030 - 0.0050 cm/cm	0.0030 - 0.0050 in/in	on Tensile Bar; SABIC Method
Melt Index of Compound	5.0 g/10 min @Load 5.00 kg, Temperature 360 Â°C	5.0 g/10 min @Load 11.0 lb, Temperature 680 Â°F	MVR [cm^3/10 min]; ISO 1133

Mechanical Properties	Metric	English	Comments
Hardness, H358/30	145 MPa	21000 psi	ISO 2039-1
Tensile Strength at Break	135 MPa	19600 psi	5 mm/min; ISO 527
Elongation at Break	3.0 %	3.0 %	5 mm/min; ISO 527
Tensile Modulus	7.20 GPa	1040 ksi	1 mm/min; ISO 527
Flexural Strength	180 MPa	26100 psi	2 mm/min; ISO 178
Flexural Modulus	5.80 GPa	841 ksi	2 mm/min; ISO 178
Izod Impact, Unnotched (ISO)	40.0 kJ/mÂ²	19.0 ft-lb/inÂ²	80104; ISO 180/1U
	40.0 kJ/mÂ² @Temperature -30.0 Â°C	19.0 ft-lb/inÂ² @Temperature -22.0 Â°F	80104; ISO 180/1U

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	20.0 Âµm/m-Â°C @Temperature 23.0 - 150 Â°C	11.1 Âµin/in-Â°F @Temperature 73.4 - 302 Â°F	ISO 11359-2
CTE, linear, Transverse to Flow	50.0 Âµm/m-Â°C @Temperature 23.0 - 150 Â°C	27.8 Âµin/in-Â°F @Temperature 73.4 - 302 Â°F	ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi)	210 Â°C	410 Â°F	Edgew 120104 sp=100mm; ISO 75/Be
Deflection Temperature at 1.8 MPa (264 psi)	205 Â°C	401 Â°F	Edgew 120104 sp=100mm; ISO 75/Ae
Vicat Softening Point	220 Â°C	428 Â°F	Rate B/50; ISO 306
	222 Â°C	432 Â°F	Rate B/120; ISO 306
	225 Â°C	437 Â°F	Rate A/50; ISO 306
Glass Transition Temp, Tg	225 Â°C	437 Â°F
UL RTI, Electrical	105 Â°C	221 Â°F	UL 746B
UL RTI, Mechanical with Impact	105 Â°C	221 Â°F	UL 746B
UL RTI, Mechanical without Impact	105 Â°C	221 Â°F	UL 746B
Flammability, UL94	V-0 @Thickness 1.50 mm	V-0 @Thickness 0.0591 in	UL 94
	5VA @Thickness 1.50 mm	5VA @Thickness 0.0591 in	UL 94
Oxygen Index	47 %	47 %	ISO 4589
Glow Wire Test	960 Â°C @Thickness 3.20 mm	1760 Â°F @Thickness 0.126 in	IEC 60695-2-12

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+15 ohm-cm	1.00e+15 ohm-cm	IEC 60093
Surface Resistance	>= 1.00e+15 ohm	>= 1.00e+15 ohm	ROA; IEC 60093
Dielectric Constant	3.0 @Frequency 1.00e+6 Hz	3.0 @Frequency 1.00e+6 Hz	IEC 60250
	3.2 @Frequency 50.0 - 60.0 Hz	3.2 @Frequency 50.0 - 60.0 Hz	IEC 60250
Dielectric Strength	16.0 kV/mm @Thickness 3.20 mm	406 kV/in @Thickness 0.126 in	in oil; IEC 60243-1
	26.0 kV/mm @Thickness 1.60 mm	660 kV/in @Thickness 0.0630 in	in oil; IEC 60243-1
Dissipation Factor	0.0016 @Frequency 50.0 - 60.0 Hz	0.0016 @Frequency 50.0 - 60.0 Hz	IEC 60250
	0.0043 @Frequency 1.00e+6 Hz	0.0043 @Frequency 1.00e+6 Hz	IEC 60250
Comparative Tracking Index	>= 100 V	>= 100 V	IEC 60112
	150 V	150 V	IEC 60112

Descriptive Properties	Value	Comments
Ball Pressure Test, 125Â°C +/- 2Â°C	PASSES	IEC 60695-10-2