- Polykemi AB POLYfill PPH T16020 Polypropylene Homopolymer, Mineral Reinforced
Polykemi AB POLYfill PPH T16020 Polypropylene Homopolymer, Mineral Reinforced
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 20% Talc Filler |
| Manufacturer | Polykemi AB |
| Trade Name | POLYfill |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polykemi AB POLYfill PPH T16020 Polypropylene Homopolymer, Mineral Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Polykemi AB
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | ISO 1183 |
| Filler Content | 20 % | 20 % | ±2%; Polykemi |
| Linear Mold Shrinkage | 0.010 - 0.012 cm/cm | 0.010 - 0.012 in/in | With Flow; ISO 2577 |
| 0.010 - 0.012 cm/cm | 0.010 - 0.012 in/in | Across Flow; ISO 2577 | |
| Melt Index of Compound | 16 g/10 min @Load 2.16 kg, Temperature 230 °C |
16 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | <= 34.0 MPa | <= 4930 psi | ISO/R527 |
| Elongation at Break | 25 % | 25 % | ISO/R527 |
| Elongation at Yield | 6.0 % | 6.0 % | ISO/R527 |
| Flexural Strength | <= 51.0 MPa | <= 7400 psi | ISO 178 |
| Flexural Modulus | 2.80 GPa @Temperature 23.0 °C |
406 ksi @Temperature 73.4 °F |
ISO 178 |
| Charpy Impact Unnotched | 1.80 J/cm² @Temperature -20.0 °C |
8.57 ft-lb/in² @Temperature -4.00 °F |
ISO 179 |
| 3.50 J/cm² @Temperature 23.0 °C |
16.7 ft-lb/in² @Temperature 73.4 °F |
ISO 179 | |
| Charpy Impact, Notched | 0.200 J/cm² @Temperature -20.0 °C |
0.952 ft-lb/in² @Temperature -4.00 °F |
ISO 179 |
| 0.300 J/cm² @Temperature 23.0 °C |
1.43 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 60.0 - 80.0 µm/m-°C | 33.3 - 44.4 µin/in-°F | Polykemi |
| Deflection Temperature at 0.46 MPa (66 psi) | 118 °C | 244 °F | 120°C/h; ISO 75/1 |
| Deflection Temperature at 1.8 MPa (264 psi) | 68.0 °C | 154 °F | 120°C/h; ISO 75/1 |
| Vicat Softening Point | 86.0 °C @Load 5.001 kg |
187 °F @Load 11.03 lb |
50°C/h; ISO 306 |
| 148 °C @Load 1.00 kg |
298 °F @Load 2.21 lb |
50°C/h; ISO 306 | |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| Glow Wire Test | 750 °C @Thickness 2.00 mm |
1380 °F @Thickness 0.0787 in |
IEC 695-2-1 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 205 - 260 °C | 401 - 500 °F | |
| Mold Temperature | 40.0 - 80.0 °C | 104 - 176 °F | |
| Drying Temperature | 70.0 - 80.0 °C | 158 - 176 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | in circulation dryer |
| 2 - 4 hour | 2 - 4 hour | in desiccant air dryer | |
| Injection Pressure | 40.0 - 110 MPa | 5800 - 16000 psi | |
| Back Pressure | 1.00 - 2.00 MPa | 145 - 290 psi |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Holding Pressure () | 20-40 | % of injection pressure |
| Injection Speed () | High | |
| Scratch Resistance, 10N (dL) | 3.3 | 10N Fine Structure; ISO 1518/D65 |
Users viewing this material also viewed the following:
- Solvay Specialty Polymers Amodel® AFA-6133 V0 Polyphthalamide (PPA) Resin, 33% Glass Reinforced, Dry As Molded &nbs
- Custom Resins Vexel™ E20GF45 FR , 45% Glass Reinforced, Flame Retardant PET (discontinued **)
- Arlon MT920-10#3.3-P1 0.020" (0.508 mm) Cured Self-Fusing Silicone Tape (Triangular, Unsupported) with Poly Interleave
- Huntsman MY 9634 Multifunctional Resin
- LyondellBasell Petrothene® GA601030 Linear Low Density Polyethylene
- Henkel Hysol EA 9380.05 Paste Adhesive System
- Daikin NEOFLON RP-4020 EFEP Pellets
- 3M 7952MP High Performance Adhesive Transfer Tapes with Adhesive 200MP
Copyright © lookpolymers.com All Rights Reserved