SABIC Innovative Plastics LNP THERMOCOMP MFB22S PP
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP MFB22S PP.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* MFB22S is a compound based on Polypropylene containing 10% Glass Fiber, 10% Glass Bead. Added feature of this grade is: Heat Stabilized.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.04 g/cc | 1.04 g/cc | ASTM D792 |
| Density | 1.035 g/cc | 0.03739 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.0300 % | 0.0300 % | 50% RH, 24 hrs; ASTM D570 |
| 0.0400 % | 0.0400 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | >= 0.020 cm/cm @Time 86400 sec |
>= 0.020 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.030 cm/cm @Time 86400 sec |
0.010 - 0.030 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 45.0 MPa | 6530 psi | Type I, 5 mm/min; ASTM D638 |
| 45.0 MPa | 6530 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 47.0 MPa | 6820 psi | Type I, 5 mm/min; ASTM D638 |
| Elongation at Break | 3.6 % | 3.6 % | 5 mm/min; ISO 527 |
| 4.1 % | 4.1 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 3.2 % | 3.2 % | Type I, 5 mm/min; ASTM D638 |
| 3.2 % | 3.2 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 3.25 GPa | 471 ksi | 1 mm/min; ISO 527 |
| 3.66 GPa | 531 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 70.0 MPa | 10200 psi | ISO 178 |
| Flexural Yield Strength | 73.0 MPa | 10600 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 2.77 GPa | 402 ksi | 2 mm/min; ISO 178 |
| 2.83 GPa | 410 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.520 J/cm | 0.974 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 4.06 J/cm | 7.61 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² | 1.90 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 25.0 kJ/m² | 11.9 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 7.00 J @Temperature 23.0 °C |
5.16 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 148 °C | 298 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 156 °C @Thickness 3.20 mm |
313 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 103 °C | 217 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 135 °C @Thickness 3.20 mm |
275 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- MV Labs HG700 Hg(NO3)2·xH2O Mercury(II) nitrate hydrate
- Mykroy/Mycalex MM 561 Molding Grade Glass-bonded Mica Composite
- Momentive Performance Materials Siloprenâ„¢ LSR 3286/70 Liquid Silicone Rubber - Self-Lubricating / Low Compression Set
- SABIC Innovative Plastics ULTEM 2310F PEI (Europe-Africa-Middle East)
- SABIC Innovative Plastics Valox® 780 PBT (Asia Pacific)
- SABIC Innovative Plastics NORYL NH7111E PPE+HIPS
- Cotronics Resbond™ 906 High Temperature Ceramic Adhesive, High Expansion
- ChevronTexaco ISO 320 Ultra Gear Lubricant
- Cytec (Conap) RN-1200 / EA-87 Conapoxy® Resin / Conacure® Hardener
- Lehmann & Voss LUVOCOM® 1301-8144 PPS, linear, with mineral filler
Copyright © lookpolymers.com All Rights Reserved