Polykemi AB POLYfill PPH GF3045 HC Polypropylene Homopolymer, Glass Fibre-Reinforced
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 40% Glass Fiber Filler |
| Manufacturer | Polykemi AB |
| Trade Name | POLYfill |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polykemi AB POLYfill PPH GF3045 HC Polypropylene Homopolymer, Glass Fibre-Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Polykemi AB
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.28 g/cc | 0.0462 lb/in³ | ISO 1183 |
| Filler Content | 45 % | 45 % | ±2%; Polykemi |
| Melt Index of Compound | 3.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
3.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | <= 114 MPa | <= 16500 psi | ISO/R527 |
| Elongation at Break | 4.0 % | 4.0 % | ISO/R527 |
| Elongation at Yield | 4.0 % | 4.0 % | ISO/R527 |
| Flexural Strength | <= 200 MPa | <= 29000 psi | ISO 178 |
| Flexural Modulus | 12.5 GPa @Temperature 23.0 °C |
1810 ksi @Temperature 73.4 °F |
ISO 178 |
| Charpy Impact, Notched | 0.800 J/cm² @Temperature -20.0 °C |
3.81 ft-lb/in² @Temperature -4.00 °F |
ISO 179 |
| 1.00 J/cm² @Temperature 23.0 °C |
4.76 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 160 °C | 320 °F | 120°C/h; ISO 75/1 |
| Vicat Softening Point | 166 °C @Load 1.00 kg |
331 °F @Load 2.21 lb |
|
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| Glow Wire Test | 750 °C @Thickness 2.00 mm |
1380 °F @Thickness 0.0787 in |
IEC 695-2-1 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 205 - 260 °C | 401 - 500 °F | |
| Mold Temperature | 40.0 - 80.0 °C | 104 - 176 °F | |
| Drying Temperature | 70.0 - 80.0 °C | 158 - 176 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | in circulation dryer |
| 2 - 4 hour | 2 - 4 hour | in desiccant air dryer | |
| Injection Pressure | 40.0 - 110 MPa | 5800 - 16000 psi | |
| Back Pressure | 1.00 - 2.00 MPa | 145 - 290 psi |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Holding Pressure () | 20-40 | % of injection pressure |
| Injection Speed () | High |
Users viewing this material also viewed the following:
- Ineos Nova 5810 High Impact Polystyrene (discontinued **)
- Ravago Manufacturing Americas Hylon® N1033TL Nylon 6/6 (DAM) (discontinued **)
- Lehmann & Voss LUVOCOM® 1105-8160 PEEK, with carbon fiber, lubricant modified
- SABIC Innovative Plastics NORYL SE100V PPE+HIPS (Asia Pacific)
- SABIC Innovative Plastics ULTEM CRS5201R PEI (Europe-Africa-Middle East)
- Techmer ES HiFill FR® ABS GF15 FR-2 15% Glass Filled
- Dow Nordel® NDR 46140.01 EPDM Hydrocarbon Rubber
- Barlog Plastics KEBAFLEX S 35 A.01 TPE-S, Shore A35, translucent
- Aremco Pyro-Tape™ 682-ER High Temperature Tape Single layer polyimide film with silicone adhesive
Copyright © lookpolymers.com All Rights Reserved