Polykemi AB POLYfill PP EIP12030F Polypropylene/EPDM, Mineral Reinforced
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | Polykemi AB |
| Trade Name | POLYfill |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polykemi AB POLYfill PP EIP12030F Polypropylene/EPDM, Mineral Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Polykemi AB
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.10 g/cc | 0.0397 lb/in³ | ISO 1183 |
| Filler Content | 30 % | 30 % | ±2%; Polykemi |
| Linear Mold Shrinkage | 0.0080 - 0.010 cm/cm | 0.0080 - 0.010 in/in | With Flow; ISO 2577 |
| 0.0080 - 0.010 cm/cm | 0.0080 - 0.010 in/in | Across Flow; ISO 2577 | |
| Melt Index of Compound | 12 g/10 min @Load 2.16 kg, Temperature 230 °C |
12 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | <= 26.0 MPa | <= 3770 psi | ISO/R527 |
| Elongation at Break | 16 % | 16 % | ISO/R527 |
| Elongation at Yield | 5.0 % | 5.0 % | ISO/R527 |
| Flexural Strength | <= 45.0 MPa | <= 6530 psi | ISO 178 |
| Flexural Modulus | 2.50 GPa @Temperature 23.0 °C |
363 ksi @Temperature 73.4 °F |
ISO 178 |
| Charpy Impact Unnotched | 2.40 J/cm² @Temperature -20.0 °C |
11.4 ft-lb/in² @Temperature -4.00 °F |
ISO 179 |
| NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ISO 179 | |
| Charpy Impact, Notched | 0.300 J/cm² @Temperature -20.0 °C |
1.43 ft-lb/in² @Temperature -4.00 °F |
ISO 179 |
| 1.10 J/cm² @Temperature 23.0 °C |
5.23 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 55.0 - 75.0 µm/m-°C | 30.6 - 41.7 µin/in-°F | Polykemi |
| Deflection Temperature at 0.46 MPa (66 psi) | 116 °C | 241 °F | 120°C/h; ISO 75/1 |
| Deflection Temperature at 1.8 MPa (264 psi) | 64.0 °C | 147 °F | 120°C/h; ISO 75/1 |
| Vicat Softening Point | 75.0 °C @Load 5.001 kg |
167 °F @Load 11.03 lb |
50°C/h; ISO 306 |
| 145 °C @Load 1.00 kg |
293 °F @Load 2.21 lb |
50°C/h; ISO 306 | |
| Glow Wire Test | 750 °C @Thickness 2.00 mm |
1380 °F @Thickness 0.0787 in |
IEC 695-2-1 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 230 - 250 °C | 446 - 482 °F | |
| Mold Temperature | 30.0 - 60.0 °C | 86.0 - 140 °F | |
| Drying Temperature | 70.0 - 80.0 °C | 158 - 176 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | in circulation dryer |
| 2 - 4 hour | 2 - 4 hour | in desiccant air dryer | |
| Injection Pressure | 40.0 - 70.0 MPa | 5800 - 10200 psi | |
| Back Pressure | 0.500 - 1.50 MPa | 72.5 - 218 psi |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Holding Pressure () | 20-40 | % of injection pressure |
| Injection Speed () | High | |
| Scratch Resistance, 10N (dL) | 6.9 | 10N Fine Structure; ISO 1518/D65 |
Users viewing this material also viewed the following:
- Osprey Metals 49FeCo2V Cobalt Alloy Powder (Grade 90% - 16)
- Precision Polymer Engineering Perlast® G60H Perfluoroelastomer
- Teknor Apex Flexalloy® 9800-60 Polyvinyl Chloride Elastomer
- Borealis LR4201R Polyethylene Insulation Compound, Crosslinkable
- ExxonMobil Greasrex K-170
- Eastman Tritan EX401 Copolyester
- Eurostar Starflam PX07037 PA6, Flame Retardant, Injection Molded
- Eurotec® Tecolen® HP30 NL XA80 PPHP, flame retardant, halogen free, heat stabilized, natural
Copyright © lookpolymers.com All Rights Reserved