Lehmann & Voss LUVOCOM® 1500-0871 Polysulfone, with glass spheres

Category Polymer , Thermoplastic , Polysulfone (PSU)
Manufacturer Lehmann & Voss & Co.
Trade Name LUVOCOM®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Lehmann & Voss LUVOCOM® 1500-0871 Polysulfone, with glass spheres.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Applications: Isotropic shrinkage characteristics.Chemical and hydrolysis resistance parts, non flammable.High dimensionally stable precision parts, high continuous use temperature.Control disks, cams, sliding elements and other duty parts.Information provided by Lehmann & Voss & Co.KG
Physical Properties Metric English Comments
Specific Gravity 1.46 g/cc
1.46 g/cc
ISO 1183
Water Absorption <= 0.10 %
<= 0.10 %
23°C/24h
Linear Mold Shrinkage 0.0050 - 0.010 cm/cm
0.0050 - 0.010 in/in
Mechanical Properties Metric English Comments
Tensile Stress 75.0 MPa
10900 psi
Elongation at Yield 3.5 %
3.5 %
4.7 %
4.7 %
flexural
Modulus of Elasticity 3.80 GPa
551 ksi
Flexural Strength 105 MPa
15200 psi
Flexural Modulus 3.20 GPa
464 ksi
Charpy Impact Unnotched 4.00 J/cm²
19.0 ft-lb/in²
flatwise; ISO 179 1fU
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 150 °C
302 °F
170 °C
338 °F
short term
Electrical Properties Metric English Comments
Surface Resistance >= 1.00e+12 ohm
>= 1.00e+12 ohm
Insulation Resistance >= 1.00e+12 ohm
>= 1.00e+12 ohm
Processing Properties Metric English Comments
Processing Temperature 355 °C
671 °F
mass temp
Nozzle Temperature 350 - 370 °C
662 - 698 °F
Zone 1 340 - 360 °C
644 - 680 °F
Zone 2 345 - 365 °C
653 - 689 °F
Zone 3 350 - 370 °C
662 - 698 °F
Mold Temperature 140 - 170 °C
284 - 338 °F
Drying Temperature 140 °C

@Time 10800 - 14400 sec
284 °F

@Time 3.00 - 4.00 hour
Dehumidifying dryer
Descriptive Properties Value Comments
Color natural color (beige)