Polykemi AB POLYfill PP CIP16020FCS Polypropylene, Fast Cycle
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 20% Talc Filler |
| Manufacturer | Polykemi AB |
| Trade Name | POLYfill |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polykemi AB POLYfill PP CIP16020FCS Polypropylene, Fast Cycle.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Polykemi AB
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | ISO 1183 |
| Filler Content | 20 % | 20 % | ±2%; Polykemi |
| Linear Mold Shrinkage | 0.010 - 0.012 cm/cm | 0.010 - 0.012 in/in | With Flow; ISO 2577 |
| 0.010 - 0.012 cm/cm | 0.010 - 0.012 in/in | Across Flow; ISO 2577 | |
| Melt Index of Compound | 16 g/10 min @Load 2.16 kg, Temperature 230 °C |
16 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 68 @Time 15.0 sec |
68 @Time 0.00417 hour |
ASTM D2240 |
| Tensile Strength at Break | <= 30.0 MPa | <= 4350 psi | ISO/R527 |
| Elongation at Yield | 6.0 % | 6.0 % | ISO/R527 |
| Flexural Strength | <= 43.0 MPa | <= 6240 psi | ISO 178 |
| Flexural Modulus | 2.50 GPa @Temperature 23.0 °C |
363 ksi @Temperature 73.4 °F |
ISO 178 |
| Charpy Impact, Notched | 0.200 J/cm² @Temperature -30.0 °C |
0.952 ft-lb/in² @Temperature -22.0 °F |
ISO 179 |
| 0.400 J/cm² @Temperature 23.0 °C |
1.90 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 129 °C | 264 °F | 120°C/h; ISO 75/1 |
| Vicat Softening Point | 156 °C @Load 1.00 kg |
313 °F @Load 2.21 lb |
50°C/h; ISO 306 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| Glow Wire Test | 750 °C @Thickness 2.00 mm |
1380 °F @Thickness 0.0787 in |
IEC 695-2-1 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 230 - 260 °C | 446 - 500 °F | |
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |
| Drying Temperature | 70.0 - 80.0 °C | 158 - 176 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | in circulation dryer |
| 2 - 4 hour | 2 - 4 hour | in desiccant air dryer | |
| Injection Pressure | 40.0 - 70.0 MPa | 5800 - 10200 psi | |
| Back Pressure | 0.500 - 1.50 MPa | 72.5 - 218 psi |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Holding Pressure () | < 20 | % of injection pressure |
| Injection Speed () | Medium | |
| Scratch Resistance, 10N (dL) | 0.12 | 10N Fine Structure; ISO 1518/D65 |
Users viewing this material also viewed the following:
- Omni Plastics OmniTuff™ CPP CCF30 Copolymer Polypropylene Calcium Carbonate Filled
- Kinlead LSS12 Low Temperature Grade Heat Sealable Film (thickness: 25 µm)
- SABIC Innovative Plastics LNP STAT-KON EX99550C PEI
- Styrolution Novodur® H801 ABS / PC
- Teknor Apex UNIPRENE® 7100-80 Thermoplastic Elastomer
- Wellman Wellamid® 22LHI6 XE-N Impact Modified Nylon 66, Lubricated & Heat Stabilized
- Eastman Eastar MN004 Copolyester
- Axiall 53061A Moldings & Extrusions Flexible PVC
- C.O.I.M. LARIPUR® LPR7060 PTMG Polyether Polyurethane
- Westlake EMAC® SP2403 24% Ethylene-Methyl Acrylate Copolymer
Copyright © lookpolymers.com All Rights Reserved