- Polykemi AB POLYelast TPE Z506 Thermoplastic Elastomer, SEBS-based
Polykemi AB POLYelast TPE Z506 Thermoplastic Elastomer, SEBS-based
| Category | Polymer , Thermoplastic , Elastomer, TPE |
| Manufacturer | Polykemi AB |
| Trade Name | POLYelast |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polykemi AB POLYelast TPE Z506 Thermoplastic Elastomer, SEBS-based.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Polykemi AB
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.15 g/cc | 0.0415 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.014 - 0.020 cm/cm | 0.014 - 0.020 in/in | With Flow; ISO 2577 |
| 0.014 - 0.020 cm/cm | 0.014 - 0.020 in/in | Across Flow; ISO 2577 | |
| Melt Index of Compound | 7.0 g/10 min @Load 5.00 kg, Temperature 190 °C |
7.0 g/10 min @Load 11.0 lb, Temperature 374 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 50 @Time 15.0 sec |
50 @Time 0.00417 hour |
Polykemi |
| Tensile Strength at Break | <= 6.00 MPa | <= 870 psi | ISO/R527 |
| Elongation at Break | 725 % | 725 % | ISO/R527 |
| 100% Modulus | 0.00140 GPa | 0.203 ksi | ISO/R527 |
| 300% Modulus | 0.00250 GPa | 0.363 ksi | ISO/R527 |
| Tear Strength | 25.0 kN/m | 143 pli | D624 |
| Compression Set | 18 % @Temperature 23.0 °C, Time 259000 sec |
18 % @Temperature 73.4 °F, Time 72.0 hour |
DIN 53517 |
| 40 % @Temperature 70.0 °C, Time 86400 sec |
40 % @Temperature 158 °F, Time 24.0 hour |
DIN 53517 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 180 - 220 °C | 356 - 428 °F | |
| Mold Temperature | 20.0 - 40.0 °C | 68.0 - 104 °F | |
| Back Pressure | 0.500 - 1.50 MPa | 72.5 - 218 psi |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Holding Pressure () | Low | % of injection pressure |
| Injection Pressure | Low | |
| Injection Speed () | High |
Users viewing this material also viewed the following:
- MV Labs B560 KBF4 Potassium tetrafluoroborate
- Paratherm Corporation Paratherm™ MR Heat Transfer Fluid
- TSE Industries Millathane® 97 Millable Polyester Polyurethane Rubber, 15.0 PHR Wacker HDK N20 Filler
- Teknor Apex APEX® 90-P513A-90-NT Polyvinyl Chloride+PUR
- TSE Industries Millathane® E34 Millable Polyether Polyurethane Rubber with 4.0 PHR MBTS
- DuPont Appeel® LSR20D745 Lidding Sealant Resin
- DSM Arnite® AV2 372 PET-35% Glass Reinforced (European and Asian Grade)
- Entec Hylex® P1025L1 HB Polycarbonate
- BASF Elastollan C 75 A TPUR
Copyright © lookpolymers.com All Rights Reserved