Polykemi AB POLYblend 85 M10 PC/ABS-Blend

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer Polykemi AB
Trade Name POLYblend
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polykemi AB POLYblend 85 M10 PC/ABS-Blend.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by Polykemi AB
Physical Properties Metric English Comments
Density 1.20 g/cc
0.0434 lb/in³
ISO 1183
Filler Content 10 %
10 %
±2%; Polykemi
Melt Index of Compound 35 g/10 min

@Load 5.00 kg,
Temperature 260 °C
 35 g/10 min

@Load 11.0 lb,
Temperature 500 °F
 ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break <= 53.0 MPa
<= 7690 psi
ISO/R527
Elongation at Break 93 %
93 %
ISO/R527
Flexural Strength <= 85.0 MPa
<= 12300 psi
ISO 178
Flexural Modulus 4.10 GPa

@Temperature 23.0 °C
 595 ksi

@Temperature 73.4 °F
 ISO 178
Charpy Impact, Notched 0.700 J/cm²

@Temperature -20.0 °C
 3.33 ft-lb/in²

@Temperature -4.00 °F
 ISO 179
3.00 J/cm²

@Temperature 23.0 °C
 14.3 ft-lb/in²

@Temperature 73.4 °F
 ISO 179
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 133 °C
271 °F
120°C/h; ISO 75/1
Deflection Temperature at 1.8 MPa (264 psi) 109 °C
228 °F
120°C/h; ISO 75/1
Vicat Softening Point 124 °C

@Load 5.001 kg
 255 °F

@Load 11.03 lb
 50°C/h; ISO 306
Flammability, UL94 HB

@Thickness 1.60 mm
 HB

@Thickness 0.0630 in
Glow Wire Test 650 °C

@Thickness 2.20 mm
 1200 °F

@Thickness 0.0866 in
 IEC 695-2-1
Processing Properties Metric English Comments
Melt Temperature 240 - 280 °C
464 - 536 °F
Mold Temperature 70.0 - 100 °C
158 - 212 °F
Drying Temperature 100 - 110 °C
212 - 230 °F
Dry Time 2 - 8 hour
2 - 8 hour
in circulation dryer
2 - 8 hour
2 - 8 hour
in fresh-air dryer
2 - 8 hour
2 - 8 hour
in desiccant air dryer
Injection Pressure 90.0 - 150 MPa
13100 - 21800 psi
Back Pressure 0.500 - 1.50 MPa
72.5 - 218 psi
Descriptive Properties Value Comments
Holding Pressure () 20-50
% of injection pressure
Injection Speed () High