Teknor Apex Monprene® MP-1580 Thermoplastic Elastomer
| Category | Polymer , Thermoplastic , Elastomer, TPE |
| Manufacturer | Teknor Apex Company |
| Trade Name | MONPRENE® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Teknor Apex Monprene® MP-1580 Thermoplastic Elastomer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Uses: Closures; Consumer Applications; Gaskets; Handles; Kitchenware; Medical/Healthcare Applications; Packaging; Safety Equipment; Sporting Goods; Toothbrush Handles; Tubing; Writing Instruments Forms: Pellets Processing Method: Extrusion; Injection Molding Injection Notes: Drying is not necessary. However, if moisture is a problem, dry the pellets for 2 to 4 hours at 150°F (65°C); Injection Rate: Fast Extrusion Notes: Screw Speed: 30 to 100 rpmInformation Provided by Teknor Apex
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.880 g/cc | 0.880 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.020 cm/cm | 0.020 in/in | ASTM D955 |
| Melt Flow | 1.00 g/10 min @Load 5.00 kg, Temperature 200 °C |
1.00 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 37 | 37 | ASTM D2240 |
| Tensile Strength at Break | 8.27 MPa | 1200 psi | ASTM D412 |
| Tensile Stress | 2.07 MPa @Strain 300 % |
300 psi @Strain 300 % |
ASTM D412 |
| Elongation at Break | 700 % | 700 % | ASTM D412 |
| Compression Set | 20 % @Temperature 22.8 °C, Time 79200 sec |
20 % @Temperature 73.0 °F, Time 22.0 hour |
ASTM D395 |
| 60 % @Temperature 70.0 °C, Time 79200 sec |
60 % @Temperature 158 °F, Time 22.0 hour |
ASTM D395 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 182 - 232 °C | 360 - 450 °F | |
| Middle Barrel Temperature | 188 - 238 °C | 370 - 460 °F | |
| Front Barrel Temperature | 193 - 243 °C | 380 - 470 °F | |
| Nozzle Temperature | 199 - 249 °C | 390 - 480 °F | |
| Zone 1 | 182 - 232 °C | 360 - 450 °F | |
| Zone 2 | 188 - 238 °C | 370 - 460 °F | |
| Zone 3 | 193 - 243 °C | 380 - 470 °F | |
| Zone 5 | 199 - 249 °C | 390 - 480 °F | |
| Die Temperature | 199 - 249 °C | 390 - 480 °F | |
| Melt Temperature | 199 - 249 °C | 390 - 480 °F | Processing Temperature |
| Mold Temperature | 35.0 - 48.9 °C | 95.0 - 120 °F | |
| Injection Pressure | 1.38 - 5.52 MPa | 200 - 800 psi | |
| Back Pressure | 0.172 - 0.689 MPa | 25.0 - 100 psi | |
| Cushion | 0.381 - 2.54 cm | 0.150 - 1.00 in | |
| Screw Speed | 50 - 100 rpm | 50 - 100 rpm |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Appearance | Clear/Transparent |
Users viewing this material also viewed the following:
- MV Labs GA800 Ga2O3 Gallium oxide
- MetalTek MTEK 175-B Cast UNS C95410 Aluminum Bronze
- Lubriplate FGL-00 Aluminum Complex USP Mineral Oil-Based Food Machinery Grade Grease
- Teknor Apex Sinelec CCB2095 Specialty Polystyrene
- ATI Wah Chang Nb/Nb Alloy C-103
- Arlon 51344R015 0.015" (0.381 mm) Semi-Cured Silicone Rubber with Fiberglass Substrate
- Addcomp ADD-VANCE® NU 559 Nucleation masterbatch, PP based
- BASF Novolen® 1127 N Polypropylene
Copyright © lookpolymers.com All Rights Reserved