Polykemi AB POLYblend 65 M10 PC/ABS-blend, Reinforced

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Glass Fiber Filled , Polycarbonate (PC)
Manufacturer Polykemi AB
Trade Name POLYblend
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polykemi AB POLYblend 65 M10 PC/ABS-blend, Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by Polykemi AB
Physical Properties Metric English Comments
Density 1.18 g/cc
0.0426 lb/in³
ISO 1183
Filler Content 10 %
10 %
±2%; Polykemi
Melt Index of Compound 25 g/10 min

@Load 5.00 kg,
Temperature 260 °C
 25 g/10 min

@Load 11.0 lb,
Temperature 500 °F
 ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break <= 48.0 MPa
<= 6960 psi
ISO/R527
Elongation at Break 109 %
109 %
ISO/R527
Flexural Strength <= 85.0 MPa
<= 12300 psi
ISO 178
Flexural Modulus 3.90 GPa

@Temperature 23.0 °C
 566 ksi

@Temperature 73.4 °F
 ISO 178
Charpy Impact, Notched 0.750 J/cm²

@Temperature -20.0 °C
 3.57 ft-lb/in²

@Temperature -4.00 °F
 ISO 179
3.20 J/cm²

@Temperature 23.0 °C
 15.2 ft-lb/in²

@Temperature 73.4 °F
 ISO 179
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 125 °C
257 °F
120°C/h; ISO 75/1
Deflection Temperature at 1.8 MPa (264 psi) 98.0 °C
208 °F
120°C/h; ISO 75/1
Vicat Softening Point 110 °C

@Load 5.001 kg
 230 °F

@Load 11.03 lb
 50°C/h; ISO 306
Flammability, UL94 HB

@Thickness 1.60 mm
 HB

@Thickness 0.0630 in
Processing Properties Metric English Comments
Melt Temperature 240 - 280 °C
464 - 536 °F
Mold Temperature 70.0 - 100 °C
158 - 212 °F
Drying Temperature 100 - 110 °C
212 - 230 °F
Dry Time 2 - 8 hour
2 - 8 hour
in circulation dryer
2 - 8 hour
2 - 8 hour
in fresh-air dryer
2 - 8 hour
2 - 8 hour
in desiccant air dryer
Injection Pressure 90.0 - 150 MPa
13100 - 21800 psi
Back Pressure 0.500 - 1.50 MPa
72.5 - 218 psi
Descriptive Properties Value Comments
Holding Pressure () 20-50
% of injection pressure
Injection Speed () High