LG Chemical LUPOL TE5108H PP+Rubber+MF, High Impact
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Mineral Reinforced, Impact Modified |
| Manufacturer | LG Chemical |
| Trade Name | LUPOL |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical LUPOL TE5108H PP+Rubber+MF, High Impact.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Injection Molding, PP+Rubber+MF, High Impact, Good WeatherabilityApplication: Automotive Exterior (Bumper Fascia, Rear Bumper Step)Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.960 g/cc | 0.960 g/cc | ASTM D792 |
| Maximum Moisture Content | 0.010 | 0.010 | Injection Molding |
| Linear Mold Shrinkage, Flow | 0.0090 - 0.010 cm/cm @Thickness 3.20 mm |
0.0090 - 0.010 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 19 g/10 min @Load 2.16 kg, Temperature 230 °C |
19 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 14.7 MPa @Thickness 3.20 mm |
2130 psi @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Elongation at Break | 300 % @Thickness 3.20 mm |
300 % @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Flexural Yield Strength | 19.6 MPa @Thickness 6.40 mm |
2840 psi @Thickness 0.252 in |
10mm/min; ASTM D790 |
| Flexural Modulus | 1.08 GPa @Thickness 6.40 mm |
156 ksi @Thickness 0.252 in |
10mm/min; ASTM D790 |
| Izod Impact, Notched | >= 0.785 J/cm @Thickness 6.40 mm, Temperature -30.0 °C |
>= 1.47 ft-lb/in @Thickness 0.252 in, Temperature -22.0 °F |
ASTM D256 |
| >= 4.90 J/cm @Thickness 6.40 mm, Temperature 23.0 °C |
>= 9.18 ft-lb/in @Thickness 0.252 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C @Thickness 6.40 mm |
239 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 190 - 210 °C | 374 - 410 °F | Injection Molding |
| Middle Barrel Temperature | 200 - 230 °C | 392 - 446 °F | Injection Molding |
| Front Barrel Temperature | 200 - 230 °C | 392 - 446 °F | Injection Molding |
| Nozzle Temperature | 210 - 230 °C | 410 - 446 °F | Injection Molding |
| Melt Temperature | 200 - 230 °C | 392 - 446 °F | Injection Molding |
| Mold Temperature | 40.0 - 60.0 °C | 104 - 140 °F | Injection Molding |
| Drying Temperature | 70.0 - 80.0 °C | 158 - 176 °F | Injection Molding |
| Dry Time | 3.00 - 4.00 hour | 3.00 - 4.00 hour | Injection Molding |
| Back Pressure | 29.4 - 58.8 MPa | 4260 - 8530 psi | Injection Molding |
| Screw Speed | 30 - 60 rpm | 30 - 60 rpm | Injection Molding |
Users viewing this material also viewed the following:
- Abatron AboCast 8-18/Abocure 8-18 Epoxy (discontinued **)
- Saint-Gobain Meldin® 8100 and 9000 Self-Lubricating Polyimide
- Sinotek Materials B Graphite Roll
- SABIC Innovative Plastics Valox® 815F PBT+PET (Asia Pacific)
- Formosa Plastics Formolene® 6144O Impact Copolymer Polypropylene
- Zylog Hipolyene® 6131 XF Thermoplastic Polyolefin & PP Compound
- TSE Industries Millathane® 97 Millable Polyester Polyurethane Rubber, 5.0 PHR Wacker HDK N20 Filler
- Axiall 38702 Coax & Telecom Flexible PVC
Copyright © lookpolymers.com All Rights Reserved