- Techmer ES Luriblend® PA6/6 CF30 TL12 30% Carbon Filled
Techmer ES Luriblend® PA6/6 CF30 TL12 30% Carbon Filled
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Carbon Fiber/PTFE Filled |
| Manufacturer | Techmer ES |
| Trade Name | Luriblend® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Techmer ES Luriblend® PA6/6 CF30 TL12 30% Carbon Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Availability: North AmericaForms: PelletsFiller/Reinforcement: Carbon Fiber, 30% Filler by WeightAdditive: PTFE + Silicone Lubricant(15%)Features: Lubricated and Good Wear ResistanceTPCI# 6466101Information provided by TP Composites, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.35 g/cc | 0.0488 lb/in³ | ASTM D792 |
| Water Absorption | 0.40 % @Time 86400 sec |
0.40 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.00050 cm/cm @Thickness 3.17 mm |
0.00050 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 200 MPa | 29000 psi | ASTM D638 |
| Elongation at Yield | 1.6 % | 1.6 % | ASTM D638 |
| Flexural Yield Strength | 306 MPa | 44400 psi | ASTM D790 |
| Flexural Modulus | 18.6 GPa | 2700 ksi | ASTM D790 |
| Izod Impact, Notched | 0.961 J/cm @Thickness 3.17 mm |
1.80 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Izod Impact, Unnotched | 7.47 J/cm @Thickness 3.17 mm |
14.0 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Coefficient of Friction, Dynamic | 0.10 | 0.10 | ASTM D1894 |
| Coefficient of Friction, Static | 0.090 | 0.090 | ASTM D1894 |
| K (wear) Factor | 16.1 x 10-8 mm³/N-M | 8.00 x 10-10 in³-min/ft-lb-hr | |
| Limiting Pressure Velocity | 0.771 MPa-m/sec | 22000 psi-ft/min | 1000 fpm |
| 1.05 MPa-m/sec | 30000 psi-ft/min | 10 fpm | |
| 1.54 MPa-m/sec | 44000 psi-ft/min | 100 fpm |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 27.0 µm/m-°C | 15.0 µin/in-°F | ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 249 °C | 480 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 10 ohm-cm | 10 ohm-cm | ASTM D257 |
Users viewing this material also viewed the following:
- KKPC KOSYN KSL 601 Styrene-Butadiene Latex
- KaMin Hydrasperse® Kaolin Clay - Filler
- Stir SpA AF 90/1 (PVC)
- SK Chemicals SKYTHANE® 175A S series Polyurethane
- A. Schulman POLYBATCH™ Blue Tint P40530 Concentrate Based In Homopolymer Polypropylene
- Tipco Tipcolene® TPE 1000 - Impact Modified Polypropylene Copolymer Compound with High Stiffness
- Chevron Phillips Marlex® 9035 High Density Polyethylene, Injection Molding
- Fainplast Compounds Hax™ CAT 103T Catalyst for Cable Compound
- Cosmic Plastics 6120 Short Glass Fiber Filled Ortho Diallyl Phthalate Molding Compound
- Chevron Phillips Dynex™ D508D7 Enhanced LLDPE Blown Film Resin (discontinued **)
Copyright © lookpolymers.com All Rights Reserved