PolyOne LubriOne™ NI-0920063 NATURAL Polyamide 610 (Nylon 610)

Category	Polymer , Thermoplastic , Nylon , Nylon 610
Manufacturer	PolyOne Corporation
Trade Name	LubriOne™
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	PolyOne LubriOne™ NI-0920063 NATURAL Polyamide 610 (Nylon 610).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

LubriOne™ Lubricated and Wear-Resistant Compounds have been specifically formulated to be self-lubricating materials, offering low coefficient of friction and improved wear resistance properties. LubriOne compounds have been demonstrated to reduce friction, noise, vibration, heat buildup and improve product durability.Information provided by PolyOne

Physical Properties	Metric	English	Comments
Specific Gravity	1.37 g/cc	1.37 g/cc	ASTM D792
Linear Mold Shrinkage, Flow	0.0010 cm/cm	0.0010 in/in	ASTM D955

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	165 MPa	23900 psi	Type I, 5.1 mm/min; ASTM D638
Elongation at Break	3.0 %	3.0 %	Type I, 5.1 mm/min; ASTM D638
Tensile Modulus	11.0 GPa	1600 ksi	Type I, 5.1 mm/min; ASTM D638
Flexural Strength	255 MPa	37000 psi	ASTM D790
Flexural Modulus	11.0 GPa	1600 ksi	ASTM D790
Izod Impact, Notched	1.10 J/cm @Thickness 3.18 mm, Temperature 23.0 °C	2.06 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F	Injection Molded; ASTM D256A

Processing Properties	Metric	English
Melt Temperature	249 - 271 °C	480 - 520 °F
Mold Temperature	65.6 - 93.3 °C	150 - 200 °F
Drying Temperature	71.1 - 82.2 °C	160 - 180 °F
Dry Time	2.00 hour	2.00 hour

Descriptive Properties	Value	Comments
Features	Good Wear Resistance
Forms	Pellets
Generic Material	Nylon 610
Generic Name	Polyamide 610 (Nylon 610)
Regional Availability	Africa & Middle East
	Asia Pacific
	Europe
	North America
	South America
Uses	Appliance Components
	Conveyor Parts
	Printer Parts