Toyobo GLAMIDE® T-400G15 Nylon-6
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 20% Glass Fiber Filled |
| Manufacturer | Toyobo |
| Trade Name | GLAMIDE® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Toyobo GLAMIDE® T-400G15 Nylon-6.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
GLAMIDE® is very tough and exhibits high abrasion resistance. It has a high melting point and heat resistance, has well-balanced proportions of mechanical properties, performs self-distinguishing and a specific grade approved as UL94V-0 class is provided, and it exhibits excellent chemical resistance and oil resistance. Grade T-400G15 is a GF reinforced Nylon-6. It contains 15% GF.15
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.25 g/cc | 1.25 g/cc | Absolute Drying; ASTM-D792 |
| Filler Content | 15 % | 15 % | |
| Water Absorption | 1.4 % | 1.4 % | Absolute Drying; ASTM-D570 |
| Moisture Absorption at Equilibrium | 3.0 % | 3.0 % | Absolute Drying; ASTM-D570 |
| Linear Mold Shrinkage | 0.0050 - 0.0070 cm/cm @Thickness 1.00 mm |
0.0050 - 0.0070 in/in @Thickness 0.0394 in |
Absolute Drying |
| 0.0070 - 0.011 cm/cm @Thickness 3.00 mm |
0.0070 - 0.011 in/in @Thickness 0.118 in |
Absolute Drying | |
| Melt Flow | 25 g/10 min | 25 g/10 min |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 118 | 118 | Absolute Drying; ASTM-D785 |
| Tensile Strength, Ultimate | 35.0 MPa @Temperature 80.0 °C |
5080 psi @Temperature 176 °F |
Practical Use (Water Absorption 3.0%); ASTM-D638 |
| 50.0 MPa @Temperature 80.0 °C |
7250 psi @Temperature 176 °F |
Absolute Drying; ASTM-D638 | |
| 60.0 MPa @Temperature 23.0 °C |
8700 psi @Temperature 73.4 °F |
Practical Use (Water Absorption 3.0%); ASTM-D638 | |
| 120 MPa @Temperature -40.0 °C |
17400 psi @Temperature -40.0 °F |
Practical Use (Water Absorption 3.0%); ASTM-D638 | |
| 120 MPa @Temperature 23.0 °C |
17400 psi @Temperature 73.4 °F |
Absolute Drying; ASTM-D638 | |
| 145 MPa @Temperature -40.0 °C |
21000 psi @Temperature -40.0 °F |
Absolute Drying; ASTM-D638 | |
| Elongation at Break | 4.0 % | 4.0 % | Absolute Drying; ASTM-D638 |
| 9.0 % | 9.0 % | Practical Use (Water Absorption 3.0%); ASTM-D638 | |
| Flexural Strength | 45.0 MPa @Temperature 80.0 °C |
6530 psi @Temperature 176 °F |
Practical Use (Water Absorption 3.0%); ASTM-D790 |
| 80.0 MPa @Temperature 23.0 °C |
11600 psi @Temperature 73.4 °F |
Practical Use (Water Absorption 3.0%); ASTM-D790 | |
| 85.0 MPa @Temperature 80.0 °C |
12300 psi @Temperature 176 °F |
Absolute Drying; ASTM-D790 | |
| 100 MPa @Temperature -40.0 °C |
14500 psi @Temperature -40.0 °F |
Practical Use (Water Absorption 3.0%); ASTM-D790 | |
| 170 MPa @Temperature 23.0 °C |
24700 psi @Temperature 73.4 °F |
Absolute Drying; ASTM-D790 | |
| 210 MPa @Temperature -40.0 °C |
30500 psi @Temperature -40.0 °F |
Absolute Drying; ASTM-D790 | |
| Flexural Modulus | 1.70 GPa @Temperature 80.0 °C |
247 ksi @Temperature 176 °F |
Practical Use (Water Absorption 3.0%); ASTM-D790 |
| 2.30 GPa @Temperature 80.0 °C |
334 ksi @Temperature 176 °F |
Absolute Drying; ASTM-D790 | |
| 2.70 GPa @Temperature 23.0 °C |
392 ksi @Temperature 73.4 °F |
Practical Use (Water Absorption 3.0%); ASTM-D790 | |
| 5.40 GPa @Temperature 23.0 °C |
783 ksi @Temperature 73.4 °F |
Absolute Drying; ASTM-D790 | |
| 5.60 GPa @Temperature -40.0 °C |
812 ksi @Temperature -40.0 °F |
Practical Use (Water Absorption 3.0%); ASTM-D790 | |
| 6.70 GPa @Temperature -40.0 °C |
972 ksi @Temperature -40.0 °F |
Absolute Drying; ASTM-D790 | |
| Compressive Strength | 110 MPa | 16000 psi | Absolute Drying; ASTM-D695 |
| Izod Impact, Notched | 0.450 J/cm @Temperature -40.0 °C |
0.843 ft-lb/in @Temperature -40.0 °F |
Absolute Drying; ASTM-D256 |
| 0.550 J/cm @Temperature -40.0 °C |
1.03 ft-lb/in @Temperature -40.0 °F |
Practical Use (Water Absorption 3.0%); ASTM-D256 | |
| 0.640 J/cm @Temperature 23.0 °C |
1.20 ft-lb/in @Temperature 73.4 °F |
Absolute Drying; ASTM-D256 | |
| 0.800 J/cm @Temperature 23.0 °C |
1.50 ft-lb/in @Temperature 73.4 °F |
Practical Use (Water Absorption 3.0%); ASTM-D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 217 °C | 423 °F | Absolute Drying; ASTM-D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 178 °C | 352 °F | Absolute Drying; ASTM-D648 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+9 ohm-cm | 1.00e+9 ohm-cm | Practical Use (Water Absorption 3.0%); ASTM-D257 |
| 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | Absolute Drying; ASTM-D257 | |
| Dielectric Strength | 17.0 kV/mm @Thickness 2.00 mm |
432 kV/in @Thickness 0.0787 in |
Practical Use (Water Absorption 3.0%); ASTM-D149 |
| 23.0 kV/mm @Thickness 2.00 mm |
584 kV/in @Thickness 0.0787 in |
Absolute Drying; ASTM-D149 | |
| Arc Resistance | 90 sec | 90 sec | Practical Use (Water Absorption 3.0%); ASTM-D495 |
| 110 sec | 110 sec | Absolute Drying; ASTM-D495 | |
| Comparative Tracking Index | 550 V | 550 V | IEC Method |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 260 - 280 °C | 500 - 536 °F | |
| Mold Temperature | 60.0 °C | 140 °F | |
| Injection Pressure | 30.0 - 55.0 MPa | 4350 - 7980 psi |
Users viewing this material also viewed the following:
- PolyOne Edgetek® NN-20CF/000 BLACK Polyamide 66 (Nylon 66)
- Kennametal Stellite Deloro® 55 Nickel Alloy
- ICO Polymers ICOFLOâ„¢ 510-5069 400 Micron LLDPE Powder
- Gromax PBT 3020-104 15% Glass Fiber Filled
- Mitsubishi Xantar® SF 2220 Polycarbonate-20% Glass Reinforced
- Styron CALIBREâ„¢ 891 10 Polycarbonate, General Purpose
- Cheng Yu Plastic VH825 Flame Retardant ABS, Medium Impact
- Fainplast Compounds GS 70/T Flexible PVC, Injection Molding for Footwear
Copyright © lookpolymers.com All Rights Reserved