- PolyOne Lubri-Tech™ PS-30GF/02S Polybutylene Terephthalate (PBT), Glass Filled, PTFE/Silicone Lubricated (dis
PolyOne Lubri-Tech™ PS-30GF/02S Polybutylene Terephthalate (PBT), Glass Filled, PTFE/Silicone Lubricated (dis
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Lubri-Tech™ PS-30GF/02S Polybutylene Terephthalate (PBT), Glass Filled, PTFE/Silicone Lubricated
(dis.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description/Features:Glass Fiber ReinforcedPTFE/Silicone LubricatedPolyOne First ChoiceInformation provided by PolyOne Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.523 g/cc | 1.523 g/cc | ASTM D792 |
| Water Absorption | 0.17 % | 0.17 % | 24 hr. Immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0020 - 0.0025 cm/cm | 0.0020 - 0.0025 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 103 MPa | 15000 psi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Tensile Modulus | 11.0 GPa | 1600 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Flexural Strength | 159 MPa | 23000 psi | ASTM D790 |
| Flexural Modulus | 11.0 GPa | 1600 ksi | ASTM D790 |
| Izod Impact, Notched | 1.33 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
2.50 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
Method A, Injection Molded; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 216 °C | 420 °F | Annealed, 0.125 in bars; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 204 °C | 400 °F | Annealed, 0.125 in bars; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 238 - 271 °C | 460 - 520 °F | Molding |
| Mold Temperature | 93.3 - 121 °C | 200 - 250 °F | |
| Drying Temperature | 93.3 °C | 200 °F | |
| Dry Time | 2 hour | 2 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Product Form | Pellets |
Users viewing this material also viewed the following:
- RheTech Products GC30P100-01UV 30% Glass Fiber Reinforced Polypropylene, Chemically Coupled, UV Stabilized, Black
- Omya OMYACARB® 10 - LU Calcium Carbonate
- Parker Chomerics CHO-SHIELD® 576 Platable Silver Epoxy Coating
- LATI Laril 13 G/30 PPOm, 30% Glass Fiber Reinforced
- A. Schulman SCHULAMID® 66 GF13 13% Glass Fiber Reinforced Nylon 66
- Polyram PlusTek PA350M6 Nylon 6.6 for Injection Molding, 30% Mineral Reinforced
- EPICHEM Epiryl B PPO Polyphenylene oxide
- Overview of materials for Linear Low Density Polyethylene (LLDPE)/Hexene, Film Grade
- A. Schulman POLYBATCH™ Grey 8035 Concentrate Based In Polyethylene
- Zircar Zirconia ZOG Single Crystal Zirconia Grog Insulation
Copyright © lookpolymers.com All Rights Reserved