Gharda Chemicals G-PAEKâ„¢ 1230CF Ultra High Performance PEK Polymer
| Category | Polymer , Thermoplastic , Polyketone , Polyaryletherketone (PAEK), Carbon Fiber Filled |
| Manufacturer | Gharda Chemicals |
| Trade Name | G-PAEK™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Gharda Chemicals G-PAEKâ„¢ 1230CF Ultra High Performance PEK Polymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Product Details: Ultra High Performance Thermoplastic material, 30% carbon fiber reinforced in Poly Aryl Ether Ketone, semi-crystalline granules suitable for injection molding, easy flow, Black in colorApplication Areas: Suitable for high temperature application, where higher strength & stiffness needed in load bearing application. Excellent wear resistance. Chemically resistant to aggressive environments, suitable for sterilization for medical and food contact applications.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.40 g/cc | 1.40 g/cc | |
| Water Absorption | 0.050 % @Time 86400 sec |
0.050 % @Time 24.0 hour |
|
| Linear Mold Shrinkage, Flow | 0.0011 cm/cm | 0.0011 in/in | 410°C nozzle, 220°C mold |
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm | 0.0080 in/in | 410°C nozzle, 220°C mold |
| Crystallinity | 40 % | 40 % | DSC |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 108 | 108 | ASTM D785 |
| Hardness, Shore D | 91 | 91 | |
| Tensile Strength, Yield | 75.0 MPa @Temperature 250 °C |
10900 psi @Temperature 482 °F |
ASTM D638 |
| 95.0 MPa @Temperature 200 °C |
13800 psi @Temperature 392 °F |
ASTM D638 | |
| 125 MPa @Temperature 150 °C |
18100 psi @Temperature 302 °F |
ASTM D638 | |
| 185 MPa @Temperature 100 °C |
26800 psi @Temperature 212 °F |
ASTM D638 | |
| 250 MPa @Temperature 23.0 °C |
36300 psi @Temperature 73.4 °F |
ASTM D638 | |
| 260 MPa @Temperature -10.0 °C |
37700 psi @Temperature 14.0 °F |
ASTM D638 | |
| 275 MPa @Temperature -50.0 °C |
39900 psi @Temperature -58.0 °F |
ASTM D638 | |
| Elongation at Break | 2.0 % | 2.0 % | ASTM D638 |
| Tensile Modulus | 22.6 GPa | 3280 ksi | ASTM D638 |
| Flexural Strength | 360 MPa | 52200 psi | ASTM D790 |
| Flexural Modulus | 22.0 GPa | 3190 ksi | ASTM D790 |
| Izod Impact, Notched | 0.500 J/cm | 0.937 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | NB | NB | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 370 - 372 °C | 698 - 702 °F | DSC |
| Deflection Temperature at 1.8 MPa (264 psi) | 368 °C | 694 °F | |
| Glass Transition Temp, Tg | 152 - 154 °C | 306 - 309 °F | DSC/onset |
| Flammability, UL94 | V-0 @Thickness 0.800 mm |
V-0 @Thickness 0.0315 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 390 - 425 °C | 734 - 797 °F | |
| Nozzle Temperature | 425 °C | 797 °F | |
| Mold Temperature | 200 - 220 °C | 392 - 428 °F | |
| Drying Temperature | 150 °C | 302 °F | |
| Dry Time | 4 - 6 hour | 4 - 6 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Hopper/ Throat Temperature | 60-80°C |
Users viewing this material also viewed the following:
- Chevron Phillips Ryton® R-4 06 PPS (Polyphenylene Sulfide) (discontinued **)
- Kingfa PBT-RG302 Flame Retardant, 30% Glass Fiber Reinforced PBT
- ExxonMobil Mobil Pegasus 805 40
- Wellman Wellamid® NY1718-N1 General Purpose Nylon 6
- Westlake Hifor LT74104 Linear Low Density Polyethylene
- ExxonMobil Mobil Vactra 4
- Fainplast Compounds Hax™ HFC 0115/1 Flame Retardant Polyolefin Cable Compound
- ConocoPhillips Hydroclear® MV100 AW Hydraulic Fluid
- Dow Corning 2-5009 Paintable Release Agent
- Colorite Polymers 7342 General Purpose Vinyl Compound
Copyright © lookpolymers.com All Rights Reserved