- SABIC Innovative Plastics Cycolac® INP576 ABS+SAN
SABIC Innovative Plastics Cycolac® INP576 ABS+SAN
| Category | Polymer , Thermoplastic , ABS Polymer |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Cycolac® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Cycolac® INP576 ABS+SAN.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Can be used as compounding additives for polymer blends. Medium molecular weight SAN. Can be blended with high rubber graft modifier resins to produce customized ABS properties. Suitable for direct weather exposure. Most versatile SAN for balance of processing and physical properties.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.08 g/cc | 1.08 g/cc | ASTM D792 |
| Density | 1.08 g/cc | 0.0390 lb/in³ | ISO 1183 |
| Melt Flow | 23 g/10 min @Load 3.80 kg, Temperature 230 °C |
23 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM D1238 |
| 78 g/10 min @Load 10.0 kg, Temperature 220 °C |
78 g/10 min @Load 22.0 lb, Temperature 428 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 122 | 122 | ASTM D785 |
| Tensile Strength at Break | 68.0 MPa | 9860 psi | Type I, 5 mm/min; ASTM D638 |
| Tensile Strength, Yield | 41.0 MPa | 5950 psi | Type I, 5 mm/min; ASTM D638 |
| Elongation at Break | 2.2 % | 2.2 % | Type I, 5 mm/min; ASTM D638 |
| Elongation at Yield | 1.4 % | 1.4 % | Type I, 5 mm/min; ASTM D638 |
| Tensile Modulus | 3.97 GPa | 576 ksi | 5 mm/min; ASTM D638 |
| Flexural Yield Strength | 68.0 MPa | 9860 psi | 2 mm/min; ISO 178 |
| 96.0 MPa | 13900 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 3.54 GPa | 513 ksi | 2 mm/min; ISO 178 |
| 3.57 GPa | 518 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.210 J/cm | 0.393 ft-lb/in | ASTM D256 |
| 0.130 J/cm @Temperature -30.0 °C |
0.244 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Izod Impact, Notched (ISO) | 1.00 kJ/m² | 0.476 ft-lb/in² | 80*10*4; ISO 180/1A |
| 1.00 kJ/m² @Temperature -30.0 °C |
0.476 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Charpy Impact Unnotched | 0.100 J/cm² | 0.476 ft-lb/in² | ISO 179/2C |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 98.0 °C @Thickness 3.20 mm |
208 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 84.0 °C | 183 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 87.0 °C @Thickness 3.20 mm |
189 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 102 °C | 216 °F | Rate B/50; ISO 306 |
| 106 °C | 223 °F | Rate B/120; ISO 306 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Yellow Index | 1.0 % | 1.0 % | ASTM D1925 |
Users viewing this material also viewed the following:
- MV Labs K910 K2HPO4 Potassium hydrogen phosphate
- Polykemi AB SCANMID 6 B60 Nylon 6, Modified
- LATI LAESTRA G/30 30% Glass Fiber Reinforced Syndiotactic Polystyrene (SPS) (discontinued **)
- LG Chemical GPPS 25SP(E) PS, High Transparency, Heat Resistance
- Ineos ABS Lustran® ABS E211 LNS013 Pellets (a-methylstyrene-SAN-modified), Extrusion Grade
- Shandong Dongyue Shenzhou New Material Co Fluorocarbon Solvent
- Teknor Apex Sarlink® 4145 Thermoplastic Elastomer
- Tra-Con Tra-Bond F175T One-Part Thixotropic UV Curing Adhesive
- AK Steel 15-5 PH® Precipitation Hardening Stainless Steel, Condition H 925
- Azoty Tarnow™ Alphalon™ E 40 L Nylon 6
Copyright © lookpolymers.com All Rights Reserved