DuPont Performance Polymers Zytel® FR70M30V0 NC010 Nylon 66  (Unverified Data**)

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Mineral Filled
Manufacturer DuPont Performance Polymers
Trade Name Zytel®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Zytel® FR70M30V0 NC010 Nylon 66  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
30% Mineral Reinforced Flame Retardant Polyamide 66 Zytel FR70M30V0 NC010 is a 30% mineral reinforced flame retardant polyamide 66 resin for injection molding.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.40 g/cc
0.0506 lb/in³
1.62 g/cc
0.0585 lb/in³
DAM; ISO 1183
Water Absorption 4.0 %

@Thickness 2.00 mm
 4.0 %

@Thickness 0.0787 in
 DAM; Sim. to ISO 62
Moisture Absorption 1.30 %

@Thickness 2.00 mm
 1.30 %

@Thickness 0.0787 in
 DAM; Sim. to ISO 62
Viscosity 67650 cP

@Shear Rate 5000 1/s,
Temperature 280 °C
 67650 cP

@Shear Rate 5000 1/s,
Temperature 536 °F
 ISO 11403-1 -2
84480 cP

@Shear Rate 5000 1/s,
Temperature 270 °C
 84480 cP

@Shear Rate 5000 1/s,
Temperature 518 °F
 ISO 11403-1 -2
107800 cP

@Shear Rate 5000 1/s,
Temperature 260 °C
 107800 cP

@Shear Rate 5000 1/s,
Temperature 500 °F
 ISO 11403-1 -2
234400 cP

@Shear Rate 500 1/s,
Temperature 280 °C
 234400 cP

@Shear Rate 500 1/s,
Temperature 536 °F
 ISO 11403-1 -2
302500 cP

@Shear Rate 500 1/s,
Temperature 270 °C
 302500 cP

@Shear Rate 500 1/s,
Temperature 518 °F
 ISO 11403-1 -2
394900 cP

@Shear Rate 500 1/s,
Temperature 260 °C
 394900 cP

@Shear Rate 500 1/s,
Temperature 500 °F
 ISO 11403-1 -2
Linear Mold Shrinkage, Flow 0.010 cm/cm
0.010 in/in
DAM; ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.010 cm/cm
0.010 in/in
DAM; ISO 294-4 2577
Mechanical Properties Metric English Comments
Tensile Strength at Break 50.0 MPa
7250 psi
50%RH; ISO 527-1/-2
73.0 MPa
10600 psi
DAM; ISO 527-1/-2
Tensile Stress 11.7 MPa

@Strain 0.880 %,
Temperature 90.0 °C
 1700 psi

@Strain 0.880 %,
Temperature 194 °F
 50%RH; ISO 11403-1 -2
12.6 MPa

@Strain 0.270 %,
Temperature 40.0 °C
 1830 psi

@Strain 0.270 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
13.1 MPa

@Strain 0.200 %,
Temperature 23.0 °C
 1900 psi

@Strain 0.200 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
14.7 MPa

@Strain 0.930 %,
Temperature 90.0 °C
 2130 psi

@Strain 0.930 %,
Temperature 194 °F
 DAM; ISO 11403-1 -2
16.9 MPa

@Strain 0.210 %,
Temperature 40.0 °C
 2450 psi

@Strain 0.210 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2
17.4 MPa

@Strain 0.170 %,
Temperature 23.0 °C
 2520 psi

@Strain 0.170 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
19.9 MPa

@Strain 0.150 %,
Temperature 0.000 °C
 2890 psi

@Strain 0.150 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2
20.3 MPa

@Strain 0.190 %,
Temperature 0.000 °C
 2940 psi

@Strain 0.190 %,
Temperature 32.0 °F
 50%RH; ISO 11403-1 -2
21.5 MPa

@Strain 0.180 %,
Temperature -20.0 °C
 3120 psi

@Strain 0.180 %,
Temperature -4.00 °F
 50%RH; ISO 11403-1 -2
25.7 MPa

@Strain 3.52 %,
Temperature 90.0 °C
 3730 psi

@Strain 3.52 %,
Temperature 194 °F
 50%RH; ISO 11403-1 -2
29.5 MPa

@Strain 6.16 %,
Temperature 90.0 °C
 4280 psi

@Strain 6.16 %,
Temperature 194 °F
 50%RH; ISO 11403-1 -2
29.6 MPa

@Strain 3.72 %,
Temperature 90.0 °C
 4290 psi

@Strain 3.72 %,
Temperature 194 °F
 DAM; ISO 11403-1 -2
30.0 MPa

@Strain 1.08 %,
Temperature 40.0 °C
 4350 psi

@Strain 1.08 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
32.9 MPa

@Strain 0.800 %,
Temperature 23.0 °C
 4770 psi

@Strain 0.800 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
33.6 MPa

@Strain 6.51 %,
Temperature 90.0 °C
 4870 psi

@Strain 6.51 %,
Temperature 194 °F
 DAM; ISO 11403-1 -2
36.9 MPa

@Strain 1.89 %,
Temperature 40.0 °C
 5350 psi

@Strain 1.89 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
39.7 MPa

@Strain 0.840 %,
Temperature 40.0 °C
 5760 psi

@Strain 0.840 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2
42.3 MPa

@Strain 1.40 %,
Temperature 23.0 °C
 6140 psi

@Strain 1.40 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
46.6 MPa

@Strain 2.00 %,
Temperature 23.0 °C
 6760 psi

@Strain 2.00 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
47.8 MPa

@Strain 1.47 %,
Temperature 40.0 °C
 6930 psi

@Strain 1.47 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2
49.8 MPa

@Strain 0.680 %,
Temperature 23.0 °C
 7220 psi

@Strain 0.680 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
51.1 MPa

@Strain 2.10 %,
Temperature 40.0 °C
 7410 psi

@Strain 2.10 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2
52.8 MPa

@Strain 0.760 %,
Temperature 0.000 °C
 7660 psi

@Strain 0.760 %,
Temperature 32.0 °F
 50%RH; ISO 11403-1 -2
53.0 MPa

@Strain 0.590 %,
Temperature 0.000 °C
 7690 psi

@Strain 0.590 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2
59.4 MPa

@Strain 0.720 %,
Temperature -20.0 °C
 8620 psi

@Strain 0.720 %,
Temperature -4.00 °F
 50%RH; ISO 11403-1 -2
64.7 MPa

@Strain 1.19 %,
Temperature 23.0 °C
 9380 psi

@Strain 1.19 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
64.7 MPa

@Strain 1.33 %,
Temperature 0.000 °C
 9380 psi

@Strain 1.33 %,
Temperature 32.0 °F
 50%RH; ISO 11403-1 -2
69.3 MPa

@Strain 1.03 %,
Temperature 0.000 °C
 10100 psi

@Strain 1.03 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2
70.9 MPa

@Strain 1.70 %,
Temperature 23.0 °C
 10300 psi

@Strain 1.70 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
77.8 MPa

@Strain 1.26 %,
Temperature -20.0 °C
 11300 psi

@Strain 1.26 %,
Temperature -4.00 °F
 50%RH; ISO 11403-1 -2
79.0 MPa

@Strain 1.47 %,
Temperature 0.000 °C
 11500 psi

@Strain 1.47 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2
86.8 MPa

@Strain 1.80 %,
Temperature -20.0 °C
 12600 psi

@Strain 1.80 %,
Temperature -4.00 °F
 50%RH; ISO 11403-1 -2
Elongation at Break 2.0 %
2.0 %
DAM; ISO 527-1/-2
6.0 %
6.0 %
50%RH; ISO 527-1/-2
Tensile Modulus 3.50 GPa
508 ksi
50%RH; ISO 527-1/-2
6.50 GPa
943 ksi
DAM; ISO 527-1/-2
Secant Modulus 1.79 GPa

@Strain 2.16 %,
Temperature 40.0 °C
 259 ksi

@Strain 2.16 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
2.78 GPa

@Strain 1.08 %,
Temperature 40.0 °C
 403 ksi

@Strain 1.08 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
2.7875 GPa

@Strain 1.60 %,
Temperature 23.0 °C
 404.30 ksi

@Strain 1.60 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
2.93 GPa

@Strain 1.68 %,
Temperature 40.0 °C
 426 ksi

@Strain 1.68 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2
4.1125 GPa

@Strain 0.800 %,
Temperature 23.0 °C
 596.48 ksi

@Strain 0.800 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
4.375 GPa

@Strain 1.52 %,
Temperature 0.000 °C
 634.5 ksi

@Strain 1.52 %,
Temperature 32.0 °F
 50%RH; ISO 11403-1 -2
4.67 GPa

@Strain 0.270 %,
Temperature 40.0 °C
 677 ksi

@Strain 0.270 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
4.73 GPa

@Strain 0.840 %,
Temperature 40.0 °C
 685 ksi

@Strain 0.840 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2
4.96 GPa

@Strain 1.36 %,
Temperature 23.0 °C
 719 ksi

@Strain 1.36 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
5.67 GPa

@Strain 1.44 %,
Temperature -20.0 °C
 823 ksi

@Strain 1.44 %,
Temperature -4.00 °F
 50%RH; ISO 11403-1 -2
6.19 GPa

@Strain 1.18 %,
Temperature 0.000 °C
 899 ksi

@Strain 1.18 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2
6.55 GPa

@Strain 0.200 %,
Temperature 23.0 °C
 950 ksi

@Strain 0.200 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
6.95 GPa

@Strain 0.760 %,
Temperature 0.000 °C
 1010 ksi

@Strain 0.760 %,
Temperature 32.0 °F
 50%RH; ISO 11403-1 -2
7.32 GPa

@Strain 0.680 %,
Temperature 23.0 °C
 1060 ksi

@Strain 0.680 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
8.05 GPa

@Strain 0.210 %,
Temperature 40.0 °C
 1170 ksi

@Strain 0.210 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2