PolyOne Lubri-Tech™ AT-15GF/10T Acetal-Copolymer, Glass Filled, PTFE Lubricated (discontinued **)
| Category | Polymer , Thermoplastic , Acetal (POM) |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Lubri-Tech™ AT-15GF/10T Acetal-Copolymer, Glass Filled, PTFE Lubricated
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description/Features:Glass Fiber ReinforcedPTFE LubricatedPolyOne First ChoiceInformation provided by PolyOne Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.57 g/cc | 1.57 g/cc | ASTM D792 |
| Water Absorption | 0.10 % | 0.10 % | 24 hr. Immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0070 - 0.0080 cm/cm | 0.0070 - 0.0080 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 75.8 MPa | 11000 psi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Elongation at Break | 4.0 % | 4.0 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Tensile Modulus | 4.83 GPa | 700 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Flexural Strength | 110 MPa | 16000 psi | ASTM D790 |
| Flexural Modulus | 4.83 GPa | 700 ksi | ASTM D790 |
| Izod Impact, Notched | 0.801 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
1.50 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
Method A, Injection Molded; ASTM D256 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 193 - 227 °C | 380 - 440 °F | Molding |
| Mold Temperature | 48.9 - 71.1 °C | 120 - 160 °F | |
| Drying Temperature | 71.1 °C | 160 °F | |
| Dry Time | 2 hour | 2 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Product Form | Pellets |
Users viewing this material also viewed the following:
- Pyrotek L8 Fiber Seal Pre-cut Gasket
- SABIC Innovative Plastics LNP STAT-KON DEL33EC PC
- Saint-Gobain COHRlastic® 8016 RFI/EMI Shielding, Electrically Conductive Impregnated Aluminum Mesh
- UBE 5034MTAX1 Nylon 6/66 Monofilament (Drawing Ratio=5)
- A. Schulman POLYFORT™ FPP 3716 Talc Filled Copolymer Polypropylene
- A. Schulman POLYBATCH™ Green P30244/4 Concentrate Based In Copolymer PP
- Axiall 7900 Moldings & Extrusions Flexible PVC
- 3M FV0164R2 Removable Vinyl Label Products
- DuPont Performance Polymers Zytel® 101L BKB009 Nylon 66 (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved