Grupo Repol Dinalon® A1X25 V0 PA66, V0 red phosphorus and halogen free
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Unreinforced, Flame Retardant |
| Manufacturer | Grupo Repol |
| Trade Name | Dinalon® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Grupo Repol Dinalon® A1X25 V0 PA66, V0 red phosphorus and halogen free.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Mechanical properties for Dry As Molded samplesInformation provided by Grupo Repol
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.18 g/cc | 0.0426 lb/in³ | ISO 1183/A |
| Moisture Absorption at Equilibrium | <= 0.25 % | <= 0.25 % | Karl-Fischer; ISO 15512/A |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 75.0 MPa | 10900 psi | ISO 527 |
| Elongation at Yield | 2.0 % | 2.0 % | ISO 527 |
| Tensile Modulus | 4.20 GPa | 609 ksi | ISO 527 |
| Flexural Strength | 110 MPa | 16000 psi | ISO 178 |
| Flexural Modulus | 2.80 GPa | 406 ksi | ISO 178 |
| Charpy Impact Unnotched | 3.00 J/cm² @Temperature 23.0 °C |
14.3 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU |
| Charpy Impact, Notched | 0.150 J/cm² @Temperature 23.0 °C |
0.714 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 80.0 °C | 176 °F | ISO 75/A |
| Vicat Softening Point | >= 200 °C | >= 392 °F | 50N; ISO 306 |
| Flammability, UL94 | V-0 @Thickness 1.60 mm |
V-0 @Thickness 0.0630 in |
|
| Glow Wire Test | 960 °C | 1760 °F | IEC 695 |
Users viewing this material also viewed the following:
- Daelim H&L Plavis G15 Aromatic Polyimide, 15% Graphite Filled, Direct Formed (Unverified Data**)
- DSM Akulon® K224-TG9/A Nylon 6-45% Glass Reinforced (European Grade) (Cond) (discontinued **)
- LG Chemical XR409H ABS, Heat Resistance
- Michelman® Release Coat® P1 Uncatalyzed portion of a two-part silicone release coating
- Shinil Chemical SHINSTRA PP SE3501 Structural Polymer Bumper
- Saint-Gobain Norton® Fluorglas® Chemfilm® DF1471 Conductive PTFE Tape
- Styrolution Terblend® N NG-04 20% Glass Filled ABS/PA6 (Dry)
- ExxonMobil 627 Mobil SHC 600 Series
- Polymer Resources PPX-FR4 Modified PPO, UL 94 V-1 with HDT of 185 F (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved