PolyOne Edgetek® PS-25MN/000 Polybutylene Terephthalate (PBT), Mineral Filled (discontinued **)
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Edgetek® PS-25MN/000 Polybutylene Terephthalate (PBT), Mineral Filled
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description/Features:Mineral FilledUL 94 HBPolyOne First ChoiceInformation provided by PolyOne Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.49 g/cc | 1.49 g/cc | ASTM D792 |
| Water Absorption | 0.080 % | 0.080 % | 24 hr. Immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.014 cm/cm | 0.014 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 60.7 MPa | 8800 psi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Elongation at Break | 4.0 % | 4.0 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Tensile Modulus | 4.21 GPa | 610 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Flexural Strength | 110 MPa | 16000 psi | ASTM D790 |
| Flexural Modulus | 4.34 GPa | 630 ksi | ASTM D790 |
| Izod Impact, Notched | 0.374 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
0.700 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
Method A, Injection Molded; ASTM D256 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 238 - 260 °C | 460 - 500 °F | Molding |
| Mold Temperature | 65.6 - 93.3 °C | 150 - 200 °F | |
| Drying Temperature | 104 °C | 220 °F | |
| Dry Time | 2 hour | 2 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Product Form | Pellets |
Users viewing this material also viewed the following:
- Plastcom SLOVASTER® B GF 30 Polybutylene Terephthalate, 30% Glass Fiber
- Polimeri Europa Clearflex® H&T LFH 208 Octene Copolymer Linear Low Density Polyethylene
- Polimeri Europa Europrene® SOL R C2525 Styrene - Butadiene Copolymer
- SABIC Innovative Plastics LNP LUBRICOMP REL22 PA 66
- Teknor Apex Monprene® MP 1107 Thermoplastic Elastomer
- Master Bond MasterSil 705C Non-Corrosive Silicone with Carbon Filler
- ExxonMobil 22M Mobilgear SHC
- BASF AMIX 100
- TSE Industries EcoWIND® P200G High Performance Filament Winding Polyurethane Resin for Pipes
- Haynes 230® alloy, as cast vacuum investment casting
Copyright © lookpolymers.com All Rights Reserved