Polyram Polytron A40B02 Nylon 66, 40% Long Fiber
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 40% Glass Fiber Filled |
| Manufacturer | Polyram |
| Trade Name | Polytron |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyram Polytron A40B02 Nylon 66, 40% Long Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
A 40% LONG FIBER GLASS REINFORCED BLACK NYLON 6.6 HEAT STABILIZED, UV STABILIZED FOR INJECTION MOLDING APPLICATION.Information provided by Polyram Ram On Ind.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.48 g/cc | 0.0535 lb/in³ | ASTM-D792 |
| Linear Mold Shrinkage | 0.0022 cm/cm | 0.0022 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 230 MPa | 33400 psi | ASTM-D638 |
| Elongation at Break | 1.9 % | 1.9 % | ASTM-D638 |
| Tensile Modulus | 13.3 GPa | 1930 ksi | ASTM-D790 |
| Flexural Strength | 340 MPa | 49300 psi | ASTM-D790 |
| Flexural Modulus | 11.2 GPa | 1620 ksi | ASTM-D790 |
| Izod Impact, Notched | 3.00 J/cm @Temperature 23.0 °C |
5.62 ft-lb/in @Temperature 73.4 °F |
ASTM-D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 255 °C | 491 °F | ASTM-D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 285 °C | 545 °F | |
| Middle Barrel Temperature | 290 °C | 554 °F | |
| Front Barrel Temperature | 300 °C | 572 °F | |
| Nozzle Temperature | 290 °C | 554 °F | |
| Melt Temperature | 300 °C | 572 °F | |
| Mold Temperature | 95.0 °C | 203 °F | |
| Injection Velocity | 50.0 - 75.0 mm/sec | 1.97 - 2.95 in/sec | |
| Moisture Content | 0.18 % | 0.18 % | |
| Back Pressure | 0.150 - 0.350 MPa | 21.8 - 50.8 psi | |
| Cushion | 0.650 cm | 0.256 in | |
| Screw Speed | 30 - 50 rpm | 30 - 50 rpm |
Users viewing this material also viewed the following:
- Proto3000 Accura® 55 Plastic Stereolithography (SLA) Prototyping Polymer
- Ravago Manufacturing Americas Hylon® N2043L Nylon 6 (DAM)
- PolyOne Edgetek® NI-10GF/000 Polyamide 610 (Nylon 610)
- Eastman Aqua 20837 PET (discontinued **)
- Lehmann & Voss LUVOCOM® 1105-7106 PEEK, with carbon fiber, PTFE, lubricant modified
- Toho Tenax Besfight® MC Type II (3000 Filament) Nickel Coated Carbon Fiber
- Dow Corning Z-1216 PHENYLTRICHLOROSILANE
- 3M 2A12 (Clear) Co-Extruded Polyethylene Protective Tapes
- Polykemi AB POLYfill PPH T5040 FC Polypropylene Homopolymer, Mineral Reinforced
- Lucent Polymers TPO-10T Thermoplastic Polyolefin, 10% Mineral Filled
Copyright © lookpolymers.com All Rights Reserved