Polymer Resources TPSF-FR1 PBT, 30% Glass Reinforced Structural Foam Grade, Flame Retardant
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 30% Glass Fiber Filled |
| Manufacturer | Polymer Resources, LTD |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polymer Resources TPSF-FR1 PBT, 30% Glass Reinforced Structural Foam Grade, Flame Retardant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Process: Foam MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Foam grades tested with foamed parts with a 10% weight reduction relative to unfoamed parts.Information provided by Polymer Resources Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.60 g/cc | 0.0578 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0020 - 0.0050 cm/cm | 0.0020 - 0.0050 in/in | ASTM D955 |
| Melt Flow | 8.0 - 18 g/10 min | 8.0 - 18 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 103 MPa | 15000 psi | ASTM D638 |
| Tensile Strength, Yield | 103 MPa | 15000 psi | ASTM D638 |
| Flexural Strength | 159 MPa | 23000 psi | ASTM D790 |
| Flexural Modulus | 6.55 GPa | 950 ksi | ASTM D790 |
| Izod Impact, Unnotched | 6.94 J/cm | 13.0 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 204 °C | 400 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 141 °C | 285 °F | ASTM D648 |
| Flammability, UL94 | HB | HB | 1/16 in |
| HB | HB | 1/8 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 238 - 254 °C | 460 - 490 °F | |
| Middle Barrel Temperature | 243 - 260 °C | 470 - 500 °F | |
| Front Barrel Temperature | 249 - 266 °C | 480 - 510 °F | |
| Melt Temperature | 232 - 260 °C | 450 - 500 °F | |
| Mold Temperature | 71.1 - 87.8 °C | 160 - 190 °F | |
| Drying Temperature | 116 - 121 °C | 240 - 250 °F | |
| Dry Time | 3 - 4 hour | 3 - 4 hour |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® 203 PC (Europe-Africa-Middle East)
- Radici Raditer® B RVA 300 Polybutylene Terephthalate with 30% Glass fiber
- NOVA Chemicals Sclair® FP020-D Octene Copolymer LLDPE Film Resin
- Gouda Vuurvast CURON 13 S Dense Refractory Castable
- Solvay Specialty Polymers Halar® 500LC Ethylene Chlorotrifluoroethylene Copolymer (ECTFE)
- Teknor Apex Telcar® TL-2560A Thermoplastic Elastomer
- Braskem LL318 LLDPE Cast Film Extrusion Polyethylene Copolymer
- A. Schulman ComAlloy Hiloy® 714 PPS, Glass Reinforced, UL
- Adell BR-33 Nylon 6, 15% Glass Reinforced
- PolyOne Synprene® RT-3605 Thermoplastic Elastomer - SBC (discontinued **)