PolyOne Edgetek® PE-10GF/000 High Density Polyethylene (HDPE), Glass Filled (discontinued **)
| Category | Polymer , Thermoplastic , Polyethylene (PE) , HDPE |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Edgetek® PE-10GF/000 High Density Polyethylene (HDPE), Glass Filled
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description/Features:Glass Fiber ReinforcedPolyOne First ChoiceInformation provided by PolyOne Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.02 g/cc | 1.02 g/cc | ASTM D792 |
| Water Absorption | 0.080 % | 0.080 % | 24 hr. Immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0050 cm/cm | 0.0050 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 57 | 57 | ASTM D785 |
| Tensile Strength, Ultimate | 31.0 MPa | 4500 psi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Elongation at Break | 4.0 % | 4.0 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Tensile Modulus | 2.41 GPa | 350 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Flexural Strength | 45.5 MPa | 6600 psi | ASTM D790 |
| Flexural Modulus | 2.41 GPa | 350 ksi | ASTM D790 |
| Compressive Strength | 34.5 MPa | 5000 psi | ASTM D695 |
| Izod Impact, Notched | 0.747 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
1.40 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
Method A, Injection Molded; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 127 °C | 260 °F | Annealed, 0.125 in bars; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 110 °C | 230 °F | Annealed, 0.125 in bars; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 188 - 221 °C | 370 - 430 °F | Molding |
| Mold Temperature | >= 26.7 °C | >= 80.0 °F | |
| Drying Temperature | 82.2 °C | 180 °F | |
| Dry Time | 2 hour | 2 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Product Form | Pellets |
Users viewing this material also viewed the following:
- Polimeri Europa SINKRAL PD H330/S ABS, Heat Stabilized (discontinued **)
- Ravago Manufacturing Americas Hylon® N1000MDHL Nylon 6/6 (discontinued **)
- Overview of materials for Nylon 66/6, 30% Glass Fiber Reinforced
- LATI Latigloss 66 H2 G/60 PA 66, 60% Glass Fiber Reinforced, Heat Stabilized
- Solvay Specialty Polymers Amodel® A-1145 HS Polyphthalamide (PPA), 45% Glass Fiber (Conditioned)
- A. Schulman CP812 Linear, Medium-Density Polyethylene
- DuPont Nucrel® 599 Ethylene-Methacrylic Acid Copolymer Resin
- Arlon T3020-B004 0.020" Self-Fusing, Cured Silicone Rubber Tape with Fiberglass Substrate
- 3M 3179 (Clear) Polyethylene Protective Tapes
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, Hardness 65A
Copyright © lookpolymers.com All Rights Reserved