A. Schulman POLYAXIS® PD8020 Polypropylene

Category	Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Molded
Manufacturer
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	A. Schulman POLYAXIS® PD8020 Polypropylene.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

DescriptionPolyaxis PD 8020 is a polypropylene designed from rotational molding with a combination of good stiffness and ESCR.NOTE: Physical properties are based on rotationally molded samples from unpigmented resin. Density and ESCR tests were performed on compression molded samples.ApplicationPolyaxis® PD 8020 is typically used in small chemical tanks and special applications. Information provided by A. Schulman.

Physical Properties	Metric	English	Comments
Specific Gravity	0.900 g/cc	0.900 g/cc	ASTM D792
ESCR 100% Igepal®	>= 1000 hour	>= 1000 hour	ASTM D1693
Melt Index of Compound	20 g/10 min	20 g/10 min	2.16/230; ASTM D1238

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	27.6 MPa	4000 psi	2"/min; ASTM D638
Elongation at Break	15 %	15 %	2"/min; ASTM D638
Flexural Modulus	1.22 GPa	177 ksi	at 1% secant modulus; ASTM D790
Impact Test	6.10 J @Thickness 3.17 mm, Temperature 23.0 °C	4.50 ft-lb @Thickness 0.125 in, Temperature 73.4 °F	ARM impact

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	85.0 °C	185 °F	ASTM D648