Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 31.0 MPa | 4500 psi | ASTM D638-95 |
Multibase Multi-Pro® 1602 S Black Polypropylene Data provided by Multibase. |
|||
Tensile Strength, Ultimate | 31.0 MPa | 4500 psi | ASTM D638-95 |
Multibase Multi-Pro® 2005 T BLK Polypropylene PP compound suitable for automotive applications, meets elevated temperature resistance. Meets ESH-M4D-293-B specifications.Data provided by Multibase. |
|||
Tensile Strength, Ultimate | 31.0 MPa | 4500 psi | ASTM D638-95 |
Multibase Multi-Pro® 4005 M I Medium Impact 40% Filler Content Polypropylene Multi-Pro 4005 M I is a chemically coupled reinforced polypropylene compound featuring high flex modulus and high impact under retention of the heat resistance properties. The product is designed f.. |
|||
Tensile Strength, Ultimate | 31.0 MPa | 4500 psi | |
Pyrotek F-51 Dense Machinable Board F-51 is a high temperature resin base, supplemented with fiberglass and graphite to provide extra strength and lubricity. F-51 is abrasion resistant and suitable for hot glass handling applications.. |
|||
Tensile Strength, Ultimate | 31.0 MPa | 4500 psi | ASTM D638 |
PolyOne Lubri-Tech™ SY-000/05T High Impact Styrene - 5% PTFE
(discontinued **) Data provided by PolyOne. |
|||
Tensile Strength, Ultimate | 31.0 MPa | 4500 psi | ASTM D412 |
Covestro Texin® DP7-3006 Thermoplastic Polyurethane, Polyether-based, Aliphatic
(discontinued **) Information provided by Bayer Corporation, Plastics DivisionAs of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and has officially adopted its new name – Covestro. This produ.. |
|||
Tensile Strength, Ultimate | 31.0 MPa | 4500 psi | ASTM D638 |
Chevron Phillips HiD® 9302 HDPE Yellow Pipe Resin
(discontinued **) Resin Type: Linear Copolymer; PE2406 Pipe Resin; ASTM D 3350 Classification: 234363E; ASTM D 4976 Classification: PE 225, A 56607Applications:Natural Gas Distribution Piping and FittingsData provide.. |
|||
Tensile Strength, Ultimate | 31.0 MPa | 4500 psi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
PolyOne Edgetek® AS-20GB/000 Acrylonitrile Butadiene Styrene (ABS), Glass Bead Filled
(discontinued **) Description/Features:Glass Bead FilledPolyOne First ChoiceInformation provided by PolyOne Corporation. |
|||
Tensile Strength, Ultimate | 31.0 MPa | 4500 psi | ASTM D638 |
NOVA Chemicals Novapol® HD-2100-A MDPE Extrusion Resin
(discontinued **) Features: Excellent ESCR and toughness, high strength, excellent processability.Applications: pipe, water pipe, fuel gas pipe, re-lining pipe, steel pipe coating.Data provided by the manufacturer. |
|||
Tensile Strength, Ultimate | 31.0 MPa @Temperature 22.0 °C |
4500 psi @Temperature 71.6 °F |
25mm flat samples, compression moulded; ISO 527-4 |
Menzolit Menzolit® BMC 0160 Unsaturated Polyester UP BMC 0160 is a general purpose BMC for electrical applications. Typical applications are lamp housings, canopies, covers and similar components.Information Provided by Menzolit |
|||
Tensile Strength, Ultimate | 31.0 MPa | 4500 psi | 2 in/min; ASTM D638 |
Ineos K38-20-188 HDPE K38-20-188 is a natural, UV stabilized, medium density polyethylene resin designed specifically for use with an approved Ineos North America yellow masterbatch to produce pipe or tubing for natural .. |
|||
Tensile Strength, Ultimate | 31.0 MPa | 4500 psi | ASTM Data |
Styron Magnum™ 2630 ABS, High Impact MAGNUM® ABS resins are thermoplastic materials which provide an excellent balance of processability, impact resistance and heat resistance as imparted by the various polymer compositions. MAGNUM .. |
|||
Tensile Strength, Ultimate | 31.0 MPa | 4500 psi | ASTM Data |
Styron Magnum™ 9035 ABS, High Gloss MAGNUM® ABS resins are thermoplastic materials which provide an excellent balance of processability, impact resistance and heat resistance as imparted by the various polymer compositions. MAGNUM .. |
|||
Tensile Strength, Ultimate | 31.0 MPa | 4500 psi | 2 in/min, at max load; ASTM D638 |
A. Schulman POLYPUR™ FPU 1152C Thermoplastic Polyurethane Information provided by A. Schulman. |
|||
Tensile Strength, Ultimate | 31.0 MPa | 4500 psi | ISO 527-1, 2 |
Polyplastics Duracon® TD-30 Acetal Co-polymer (POM), High impact, Flexible DURACON® is a crystalline thermoplastic acetal copolymer. The primary raw material trioxane, a trimer of formaldehyde.The thermoplastic adopts a copolymer structure in which polyoxymethylene (-C-O).. |
|||
Tensile Strength, Ultimate | 31.0 MPa | 4500 psi | at max load; ASTM D638 |
A. Schulman POLYPUR™ FPU 1103F Thermoplastic Polyurethane Compound Information provided by A. Schulman. |
|||
Tensile Strength, Ultimate | 31.0 MPa | 4500 psi | ASTM D638 |
Eastman Tenite Propionate 381E4000015 Clear, Trsp Cellulose Acetate Propionate Plasticizer 15%. Weight loss on heating = 0.7% per ASTM D 707. Soluble matter loss = 0.1% per ASTM D 570.Product Description: TENITE cellulosic plastics are noted for their excellent balance of p.. |
|||
Tensile Strength, Ultimate | 31.0 MPa | 4500 psi | ASTM D638 |
Ecomass® 1050CO94 Copper Filled Polyamide Nontoxic alternative to Lead (Pb), weighting and balancing applicationsModerate Specific GravityCopper Powder Filled Polyamide (PA) AlloyGood ToughnessInformation provided by Technical Polymers |
|||
Tensile Strength, Ultimate | 31.0 - 37.2 MPa | 4500 - 5400 psi | Polypropylene; ASTM D638M |
DSM Somos® 9120 The need for movable parts is a constant when it comes to prototyping. Being able to ensure the proper fit for parts within a component can save both time and money. Somos® 9120 creates semi-transp.. |
|||
Tensile Strength, Ultimate | 31.0 MPa | 4500 psi | ASTM D638 |
DuPont™ Surlyn® 8020 Ionomer Resin, Sodium Surlyn® 8020 thermoplastic resin is an advanced ethylene/methacrylic acid (E/MAA) copolymer, in which the MAA acid groups have been partially neutralized with sodium ions. The amount of MAA and neu.. |
|||
Tensile Strength, Ultimate | 31.0 MPa | 4500 psi | ASTM D412 |
BASF Elastollan® S80A Polyester Type Polyurethane Elastomer Processed by extrusion or injection molding. Elastollan S series of products are polyester-based thermoplastic polyurethanes that exhibit good hydrolytic stability. They also exhibit good oil, fue.. |
|||
Tensile Strength, Ultimate | 31.0 MPa | 4500 psi | after optimum cure |
Armstrong X-6/E Epoxy Adhesive Thixotropic.Information provided by Ellsworth Adhesives. |
|||
Tensile Strength, Ultimate | 31.0 MPa | 4500 psi | ASTM D638-95 |
Multibase Multi-ABS 3522 Utility Grade Multi-ABS 3522 utility grade is a black ABS resin produced for wide-specs and recycled resins. This product is suitable for automotive application and for non-critical load bearing parts.Data provid.. |
|||
Tensile Strength, Ultimate | 31.0 MPa | 4500 psi | ASTM D638-95 |
Multibase Multi-ABS 3525 Clear Data provided by Multibase. |
|||
Tensile Strength, Ultimate | 31.0 - 128 MPa | 4500 - 18500 psi | Average value: 79.1 MPa Grade Count:17 |
Overview of materials for Acrylonitrile Butadiene Styrene (ABS)/Nylon Blend, Glass Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Acrylonitrile Butadiene Styrene (ABS)/Nylon Blend, Glass Reinforced". Each property range of values repo.. |
|||
Tensile Strength, Ultimate | 31.0 - 43.0 MPa @Temperature 180 - 180 °C |
4500 - 6240 psi @Temperature 356 - 356 °F |
Average value: 68.8 MPa Grade Count:1 |
Overview of materials for Polyethersulfone (PES) This property data is a summary of similar materials in the MatWeb database for the category "Polyethersulfone". Each property range of values reported is minimum and maximum values of appropriate M.. |
|||
Tensile Strength, Ultimate | 31.0 - 43.0 MPa @# of Cycles 100000 - 1.00e+7 |
4500 - 6240 psi @# of Cycles 100000 - 1.00e+7 |
Average value: 68.8 MPa Grade Count:1 |
Overview of materials for Polyethersulfone (PES) This property data is a summary of similar materials in the MatWeb database for the category "Polyethersulfone". Each property range of values reported is minimum and maximum values of appropriate M.. |
|||
Tensile Strength, Ultimate | 31.0 - 43.0 MPa @Temperature 180 - 180 °C |
4500 - 6240 psi @Temperature 356 - 356 °F |
Average value: 70.2 MPa Grade Count:1 |
Overview of materials for Polyethersulfone (PES), 30% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyethersulfone (PES), 30% Glass Fiber Filled". Specific grades with glass content between 25% and 34% .. |
|||
Tensile Strength, Ultimate | 31.0 MPa | 4500 psi | ASTM D412-80 |
DuPont Performance Polymers Hypalon® 4085 Chlorosulfonated Polyethylene Rubber, Gum Compound
(discontinued ** Gum compound with 100 parts Hypalon; 4 parts high activity magnesia; 3 parts pentaerythritol; and 2 parts Tetrone® A rubber accelerator (from DuPont Dow Elastomers). Reinforcing fillers not needed.. |