Precision Polymer Engineering Z85L Hydrogenated NBR Compound

Category	Polymer , Thermoset , Rubber or Thermoset Elastomer (TSE)
Manufacturer	Precision Polymer Engineering Limited
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Precision Polymer Engineering Z85L Hydrogenated NBR Compound.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Peroxide Cured, Hydrogenated Nitrile Rubber, 81-90 °IRHD. Low acrylonitrile content.Applications: Specially compounded for service in low-temperature applications. High strength and excellent chemical resistance. Higher operating temperature than standard nitrile. Suitable for use with sour (H2S) crude oil and gas, which may also include lubricating, oil additives and amine corrosion inhibitors. Good resistance to weathering and ozone.

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	85	85	°IRHD; ASTM D1415
	94	94	°IRHD, +9 change after 70 hours @ 150°C; ASTM D1415
Tensile Strength, Yield	18.3 MPa	2650 psi	ASTM D412
	20.13 MPa	2920 psi	10% change after 70 hours @ 150°C; ASTM D412
Elongation at Break	165.75 %	165.75 %	-15% change after 70 hours @ 150°C; ASTM D412
	195 %	195 %	ASTM D412
Compression Set	21 %	21 %	24 hours @ 150°C; ASTM D395

Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Air	180 °C	356 °F
Minimum Service Temperature, Air	-30.0 °C	-22.0 °F
	-30.0 °C	-22.0 °F	Non-brittle after 3 minutes
Flash Point	>= 300 °C	>= 572 °F