- Lucent Polymers PC/PBT-1420IM Polycarbonate+PBT, Superior Cold Temp Impact, Injection Grade
Lucent Polymers PC/PBT-1420IM Polycarbonate+PBT, Superior Cold Temp Impact, Injection Grade
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/Polybutylene Terephthalate (PBT) Blend, Unreinforced , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | Lucent Polymers |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lucent Polymers PC/PBT-1420IM Polycarbonate+PBT, Superior Cold Temp Impact, Injection Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Add "R" for Added ReleaseAdd "U" for UV StabilizerInformation provided by Lucent Polymers, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.17 g/cc | 1.17 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.011 cm/cm @Thickness 3.17 mm |
0.011 in/in @Thickness 0.125 in |
1/8" Section |
| Melt Flow | 20 g/10 min @Load 5.00 kg, Temperature 260 °C |
20 g/10 min @Load 11.0 lb, Temperature 500 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 48.97 MPa | 7103 psi | ASTM D638 |
| Elongation at Break | >= 168 % | >= 168 % | ASTM D638 |
| Flexural Strength | 68.97 MPa | 10000 psi | ASTM D790 |
| Flexural Modulus | 1.710 GPa | 248.1 ksi | ASTM D790 |
| Izod Impact, Notched | 5.34 J/cm @Thickness 3.17 mm, Temperature -30.0 °C |
10.0 ft-lb/in @Thickness 0.125 in, Temperature -22.0 °F |
ASTM D256 |
| 7.48 J/cm @Thickness 3.17 mm, Temperature 22.8 °C |
14.0 ft-lb/in @Thickness 0.125 in, Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 97.78 °C | 208.0 °F | ASTM D648 |
Users viewing this material also viewed the following:
- Nylene® PA6/6 Impact Modified 311 HS Nylon 6/6
- Orion Engineered Carbons CORAX® N 550 ASTM Carbon Black
- SABIC Innovative Plastics Cycolac® X37 ABS (Europe-Africa-Middle East)
- SABIC Innovative Plastics LNP LUBRICOMP DFI14 PC
- Techmer ES Electrablend® PC SS15 FR BK 15% Stainless Steel Filled
- ExxonMobil 422 Mobilmet 400 Series
- Polyram RamTal PM8427 Acetal, Impact modified
- A. Schulman POLYFORT™ FXP 1943 CaC03 and Glass Fiber Hybrid Copolymer Polypropylene
- Adell EA-14 Homopolymer Polypropylene, 20% Talc Filled
- ATI Allegheny Ludlum Stainless Steel Chromium-Nickel Type 302, 60% Cold Rolled (UNS S30200)
Copyright © lookpolymers.com All Rights Reserved