PolyOne Bergamid™ A70 G35 H U BK SO Polyamide 66 (Nylon 66)

Category Polymer , Thermoplastic , Nylon , Nylon 66
Manufacturer PolyOne Corporation
Trade Name Bergamid™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF PolyOne Bergamid™ A70 G35 H U BK SO Polyamide 66 (Nylon 66).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by PolyOne
Physical Properties Metric English Comments
Density 1.50 g/cc
0.0542 lb/in³
ISO 1183
Linear Mold Shrinkage 0.0030 - 0.0050 cm/cm

@Thickness 4.00 mm,
Temperature 23.0 °C
 0.0030 - 0.0050 in/in

@Thickness 0.157 in,
Temperature 73.4 °F
 Flow Mold Shrinkage on Tensile Bar, flow Bergmann Method; ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength at Break 130 MPa

@Thickness 4.00 mm,
Temperature 23.0 °C
 18900 psi

@Thickness 0.157 in,
Temperature 73.4 °F
 ISO 527-2
Elongation at Break 2.0 %

@Thickness 4.00 mm,
Temperature 23.0 °C
 2.0 %

@Thickness 0.157 in,
Temperature 73.4 °F
 ISO 527-2
Tensile Modulus 12.0 GPa

@Thickness 4.00 mm,
Temperature 23.0 °C
 1740 ksi

@Thickness 0.157 in,
Temperature 73.4 °F
 ISO 527-2
Charpy Impact Unnotched 4.00 J/cm²

@Temperature -30.0 °C
 19.0 ft-lb/in²

@Temperature -22.0 °F
 ISO 179
5.00 J/cm²

@Temperature 23.0 °C
 23.8 ft-lb/in²

@Temperature 73.4 °F
 Injection Molded; ISO 179
Charpy Impact, Notched 0.550 J/cm²

@Temperature -30.0 °C
 2.62 ft-lb/in²

@Temperature -22.0 °F
 ISO 179
0.750 J/cm²

@Temperature 23.0 °C
 3.57 ft-lb/in²

@Temperature 73.4 °F
 ISO 179
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 236 °C
457 °F
Annealed; ISO 75-2/A
Flammability, UL94 V-0

@Thickness 0.800 mm
 V-0

@Thickness 0.0315 in
 ALL; UL 94
V-0

@Thickness 1.60 mm
 V-0

@Thickness 0.0630 in
 ALL; UL 94
V-0

@Thickness 3.20 mm
 V-0

@Thickness 0.126 in
 ALL; UL 94
Glow Wire Test 960 °C

@Thickness 0.800 mm
 1760 °F

@Thickness 0.0315 in
 Flammability Index; IEC 60695-2-12
960 °C

@Thickness 3.00 mm
 1760 °F

@Thickness 0.118 in
 Flammability Index; IEC 60695-2-12
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
IEC 60093
Surface Resistance 1.00e+13 ohm
1.00e+13 ohm
IEC 60093
Comparative Tracking Index 600 V
600 V
IEC 60112
Processing Properties Metric English Comments
Melt Temperature 260 - 280 °C
500 - 536 °F
Mold Temperature 65.0 - 85.0 °C
149 - 185 °F
Drying Temperature 80.0 - 90.0 °C
176 - 194 °F
Dry Time 4.00 hour
4.00 hour
Descriptive Properties Value Comments
Additive Heat Stabilizer
Features Flame Retardant
Filler / Reinforcement Glass Fiber Reinforcement, 35% Filler by Weight
Forms Pellets
Generic Material Nylon 66
Generic Name Polyamide 66 (Nylon 66)
Processing Method Injection Molding
Regional Availability Europe
RoHS Compliance RoHS Compliant