SABIC Innovative Plastics LNP LUBRICOMP WFP36 PBT (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP WFP36 PBT (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP LUBRICOMP* WFP36 is a compound based on Polybutylene Terephalate resin containing Silicone, Glass Fiber, PTFE. Added features of this material include: Internally Lubricated.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.57 g/cc | 0.0567 lb/in³ | ISO 1183 |
| 1.579 g/cc | 0.05704 lb/in³ | ASTM D792 | |
| Moisture Absorption | 0.400 % | 0.400 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm @Time 86400 sec |
0.0010 - 0.0030 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0010 - 0.0030 cm/cm @Time 86400 sec |
0.0010 - 0.0030 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0050 - 0.010 cm/cm @Time 86400 sec |
0.0050 - 0.010 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0050 - 0.010 cm/cm @Time 86400 sec |
0.0050 - 0.010 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 113 MPa | 16400 psi | ASTM D638 |
| 118 MPa | 17100 psi | ISO 527 | |
| Elongation at Break | 2.5 % | 2.5 % | ASTM D638 |
| 2.7 % | 2.7 % | ISO 527 | |
| Tensile Modulus | 10.28 GPa | 1491 ksi | 50 mm/min; ASTM D638 |
| 11.76 GPa | 1706 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 189 MPa | 27400 psi | ISO 178 |
| 193 MPa | 28000 psi | ASTM D790 | |
| Flexural Modulus | 8.74 GPa | 1270 ksi | ASTM D790 |
| 9.35 GPa | 1360 ksi | ISO 178 | |
| Izod Impact, Notched | 0.690 J/cm | 1.29 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 5.76 J/cm | 10.8 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² | 4.76 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 46.0 kJ/m² | 21.9 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 7.00 J | 5.16 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 14.0 J | 10.3 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.50 | 0.50 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.42 | 0.42 | ASTM D3702 Modified |
| K (wear) Factor | 274 x 10-8 mm³/N-M | 136 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 213 °C | 415 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 213 °C @Thickness 3.20 mm |
415 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- MV Labs SC1000 Sc2(SO4)3·5H2O Scandium sulfate pentahydrate
- DuPont Vamac® G/HVG Sample Compound (discontinued **)
- Momentive Performance Materials Siloprenâ„¢ FSL 7641 Fluorinated Liquid Silicone Rubber
- Wellman Wellpet® FRGF116-BK1 Polyethylene Terephthalate, 30% Glass Fiber Reinforced, Flame Retardant
- Eurostar Staramide BG6U PA6, 30% Glass Fiber Filled, UV Stabilized, Injection Molded
- Beijing Evergrow Resources ER-23 UHMW PE Bulletproof Insert Plate
- 3M 5180 General Purpose PTFE Skived Film Tapes
- Gromax CCP PBT 3030-200HR 30% Glass Fiber Filled
- Victrex® PEEK 380P Polyetheretherketone, Unreinforced
Copyright © lookpolymers.com All Rights Reserved