PolyOne Bergadur™ PB40 G15 blue Polybutylene Terephthalate (PBT)
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 20% Glass Fiber Filled |
| Manufacturer | PolyOne Corporation |
| Trade Name | Bergadur™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Bergadur™ PB40 G15 blue Polybutylene Terephthalate (PBT).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by PolyOne
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.42 g/cc @Temperature 23.0 °C |
0.0513 lb/in³ @Temperature 73.4 °F |
±0.02; ISO 1183 |
| Melt Flow | 30 g/10 min @Load 2.16 kg, Temperature 250 °C |
30 g/10 min @Load 4.76 lb, Temperature 482 °F |
±5; ISO 1133 |
| Melt Index of Compound | 25 g/10 min @Load 2.16 kg, Temperature 250 °C |
25 g/10 min @Load 4.76 lb, Temperature 482 °F |
±5; cm³/10min; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 105 MPa @Thickness 4.00 mm, Temperature 23.0 °C |
15200 psi @Thickness 0.157 in, Temperature 73.4 °F |
Injection Molded; ISO 527-2 |
| Elongation at Break | >= 3.0 % @Thickness 4.00 mm, Temperature 23.0 °C |
>= 3.0 % @Thickness 0.157 in, Temperature 73.4 °F |
Injection Molded; ISO 527-2 |
| Tensile Modulus | 6.50 GPa @Thickness 4.00 mm, Temperature 23.0 °C |
943 ksi @Thickness 0.157 in, Temperature 73.4 °F |
ISO 527-2 |
| Charpy Impact Unnotched | 3.10 J/cm² @Temperature 23.0 °C |
14.8 ft-lb/in² @Temperature 73.4 °F |
Injection Molded; ISO 179 |
| Charpy Impact, Notched | 0.370 J/cm² @Temperature 23.0 °C |
1.76 ft-lb/in² @Temperature 73.4 °F |
Injection Molded; ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
Internal Method |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
| Surface Resistance | 1.00e+15 ohm | 1.00e+15 ohm | ASTM D257 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 240 - 260 °C | 464 - 500 °F | |
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |
| Drying Temperature | 80.0 - 120 °C | 176 - 248 °F | |
| Dry Time | 4.00 hour | 4.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Appearance | Blue | |
| Features | Good Chemical Resistance | |
| Good Impact Resistance | ||
| Filler / Reinforcement | Glass Fiber Reinforcement, 15% Filler by Weight | |
| Forms | Pellets | |
| Generic Material | PBT | |
| Generic Name | Polybutylene Terephthalate (PBT) | |
| Processing Method | Injection Molding | |
| Regional Availability | Europe | |
| RoHS Compliance | RoHS Compliant |
Users viewing this material also viewed the following:
- Niche Polymer PA66GI14BK Nylon 66, 14% Glass Fiber Filled, Impact Modified
- Polykemi AB SCANTEC PC S75R GF10 Polycarbonate, Glass Fiber Reinforced
- 3M Dyneon™ PFA 6503 C EPC Perfluoroalkoxy Fluorothermoplastic (discontinued **)
- LG Chemical LUMID GP1200A(W) PA6, Medium Viscosity
- Kotec Carbotex K-20T30 Polycarbonate, General Purpose
- KaMin KaMin® HG Kaolin Clay - Waterwashed
- Styron Buna® SB 1739 Schkopau Cold Polymerized Emulsion Styrene Butadiene Rubber (E-SBR)
- EMS-Grivory Grivory® BG-15 HM PA6-GF15
- Clariant Renol PP1112AS10 Polypropylene, Static Dissipative
- Asahi Kasei Thermylene® P6-30FM-Y249B 30% Glass/Mineral Reinforced, Heat Stabilized
Copyright © lookpolymers.com All Rights Reserved