Huntsman PE1068 Film Extrusion Polyethylene (discontinued **)
| Category | Polymer , Film , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Film Grade |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Huntsman PE1068 Film Extrusion Polyethylene
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Homopolymer and FDA compliant.Features: Exceptional draw down and processability even to 1/2 mil; excellent strength, good heat sealability, and good optical.FDA Notes: Conforms to FDA regulation 21 CFR 177.1520 (c)2.2 under condition of use B through H described in Table 2 of 21 CFR 176.170Film properties based on 1.0 guage (25 µm) thickness; blow-up ratio 2:1.Information provided by Huntsman Corporation
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.922 g/cc | 0.0333 lb/in³ | ASTM D1505 |
| Thickness | 25.4 microns | 1.00 mil | |
| Melt Flow | 5.5 g/10 min | 5.5 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 52 | 52 | ASTM D2240 |
| Tensile Strength, Ultimate | 10.0 MPa | 1450 psi | ASTM D638 |
| Tensile Strength, Yield | 10.0 MPa | 1450 psi | ASTM D638 |
| Film Elongation at Break, MD | 275 % | 275 % | ASTM D882 |
| Film Elongation at Break, TD | 400 % | 400 % | ASTM D882 |
| Elongation at Break | 400 % | 400 % | ASTM D638 |
| Modulus of Elasticity | 0.242 GPa | 35.1 ksi | Secant; ASTM D638 |
| Secant Modulus, MD | 0.159 GPa | 23.1 ksi | ASTM D882 |
| Secant Modulus, TD | 0.186 GPa | 27.0 ksi | ASTM D882 |
| Dart Drop | 1.77 g/micron | 45.0 g/mil | ASTM D1709 |
| Dart Drop Test | 45.0 g | 0.0992 lb | ASTM D1709 |
| Film Tensile Strength at Break, MD | 17.0 MPa | 2470 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 14.0 MPa | 2030 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Vicat Softening Point | 96.0 °C | 205 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 4.0 % | 4.0 % | ASTM D1003 |
| Gloss | 78 % | 78 % | at 45°; ASTM D523 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 143 - 154 °C | 289 - 309 °F |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Flexible D9000 Polyvinyl Chloride, Flexible (PVC, Flexible)
- LG Chemical Lupoy 3030-15 Polycarbonate Resin
- Iran Petrochemical (PCC) 2602TH00 Low Density Polyethylene
- Lehmann & Voss LUVOCOM® 1105/XCF/15 PEEK, with carbon fiber
- Techmer ES HiFill® PA6/6 GF60 IM HS L 60% Glass Filled (Dry)
- A. Schulman SCHULAMID® 66 PTFE20 HS 20% PTFE Lubricated, Heat Stabilized Nylon 6/6
- Chevron Phillips MarFlex® 5429 Low Density Polyethylene, Cast Film
- Braskem CP 191 Injection Molding Polypropylene
- Carpenter Gall-Tough PLUS™ Stainless, Annealed, 20% Cold Work
Copyright © lookpolymers.com All Rights Reserved